对化学镀镍-磷的镀液性能和镀层性能进行了研究。筛选了一种含稀土混合添加剂XT，从而改善了槽液的稳定性，镀层含磷量、显微硬度和韧性增加。利用试验数据推算了所研究体系沉镍反应的活化能为56kJ/mol。
Bath and deposit properties of electroless nickelphosphorus-plating were investigated. A complex additive XT containing RE was developed, which can improve the bath stability and increase phosphorus content, microhardness and durability of the nickel-phosphorus deposit. Apparent active energy of nickel-deposit reaction in the studied system was 56 kJ/mol calculated with the experiment datum.
参考文献
| [1] | 伍学高;李铭华;黄谓成.化学镀技术[M].成都:四川科学技术出版社,1985 |
| [2] | 姚红宇;聂宇 .化学镀镍的电解再生[J].电镀与环保,1993,13(02):16-18. |
| [3] | 孙景庄;薛惠茹 .提高化学镀镍层含磷量的研究[J].电镀与环保,1995,15(03):15-18. |
| [4] | 张翼;范洪富;张利均 .化学镀Ni-P的自发性及影响因素[J].电镀与环保,1996,16(06):16-18. |
| [5] | 严易舒.中温酸性化学镀镍[J].材料保护,1996(05):24. |
| [6] | 陈立佳;王赫莹;赵忠俭 等.化学镀Ni-P合金动力学的研究[J].电镀与涂饰,1997,16(02):9-12. |
| [7] | 韩克平.硫脲稳定化学镀镍的机理[J].电镀与精饰,1996(03):11. |
| [8] | 夏承钰.酸性化学镀镍沉积速度的研究[J].材料保护,1996(01):4. |
| [9] | 戴长松;吴宜勇;王殿龙 等.化学镀镍稳定性的综合评价[J].电镀与环保,1997,17(04):9-11. |
| [10] | 汤皎宁;林良海;黄令 等.稀土元素对化学镀镍的影响[J].材料保护,1997,30(03):8-10. |
| [11] | 李朝林;周定;唐彩红 .电渗析法再生化学镀镍溶液的研究[J].电镀与环保,1997,17(01):13-15. |
| [12] | 沈伟.化学镀镍的成本与价格[J].材料保护,2000(10):10-11. |
| [13] | 天津大学物化教研室.物理化学[M].北京:人民教育出版社,1979 |
| [14] | 庄瑞舫.化学镀镍磷合金技术探讨（Ⅰ）[J].材料保护,1997(09):41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%