以外观、醋酸铅点滴实验和中性盐雾实验(NSS)为评价标准,通过正交实验和单因素实验,得到了一种三价铬钝化膜的最佳工艺条件:0.1 mol/L CrCl3,0.2 mol/L有机羧酸CM,0.24 mol/L NaNO3,0.01 mol/L Co(NO3)2,8g/L Na2SiO3,pH为1.2,钝化温度为10℃,钝化时间为30 s.探讨了配合物CM浓度、硝酸钠浓度、氯化铬浓度、硝酸钴浓度、硅酸钠浓度及钝化液pH、钝化温度、钝化时间的影响.在上述条件下得到的钝化膜呈蓝色,均匀,能通过48 h NSS实验.
参考文献
| [1] | 俞雄飞.入世后过渡期如何应对国外技术性贸易壁垒[J].WTO-TBT信息与研究,2005(05):10-24. |
| [2] | 钱达人;李士嘉;何建平 等.锌的三价铬盐钝化处理初探[J].南京航空学院学报,1991,21(11):20-21. |
| [3] | Bishop Thomay .Black chromium-containing conversion coatings on zinc-nickel and zinc-iron alloys[P].US:5415702,1995-05-16. |
| [4] | L Roman;M Blidariu;C Cristescu .Study of Conversion Coatings on Zinc Deposition Obtained from LowPollution Solutions[J].Transactions of the Institute of Metal Finishing,1997,75(05):171-174. |
| [5] | R Sarmaitis;V Dikinis;V Rezaite.Conversion Coatings for Zinc Substrates from Acidic Solutions of Cr Compounds[A].:575-583. |
| [6] | GB 9791-1988.GB 9791-1988.锌和镉上铬酸盐转化膜试验方法[S]. |
| [7] | GB 6458-1986.GB 6458-1986.金属覆盖层-中性盐雾试验(NSS试验)[S]. |
| [8] | 蒲海丽,王建华,蒋雄.三价铬钝化的探讨[J].电镀与环保,2004(02):25-26. |
| [9] | Huvar .Trivalent chromiumPassivate solution andProcess[P].US:4349392,1982-09-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%