采用正交试验法优选了磷化液最佳配方为217g/L磷酸,50g/L氧化锌,40g/L磷酸二氢钠,3g/L钼酸铵,2g/L植酸,1.5g/L乙酸锰,4.5g/L氧化促进剂DJ1,1.5g/L低温促进剂DJ2,3g/L复配表面活性剂DJ3.所得磷化膜经金相显微镜观察,其金相结构致密、连续.通过电化学方法测试成膜过程的极化曲线,表明磷化过程成膜后,腐蚀电流基本保持不变.利用X射线光电子能谱测定膜表面的元素组成,发现Zn、Fe、P的不同峰值的能谱,及O的能谱峰及俄歇能谱同时存在,说明磷化膜主要是由Fe、Zn的多种磷酸盐构成.该磷化液稳定,沉渣少,成膜速度快,磷化膜耐蚀性能好.
参考文献
| [1] | Feliu S;Barranco V .Study of degradation mechanisms of a protective lacquer film formulated with phosphating reagents applied on galvanised steel, galvanneal and galfan in exposure to UV/condensation test[J].Surface & Coatings Technology,2004(2/3):251-260. |
| [2] | Deya MC.;Blustein G.;Romagnoli R.;del Amo B. .The influence of the anion type on the anticorrosive behaviour of inorganic phosphates[J].Surface & Coatings Technology,2002(2/3):133-142. |
| [3] | TRINH A T;NADINE P .Study of the synergistic observed for the corrosion protection of a carbon steel by an association of phosphates[J].Corrosion Science,2002,44:2055-2071. |
| [4] | 曾德芳,刘志明,卓海华.环保型单组分低温磷化液的研制[J].电镀与涂饰,2000(04):28-31. |
| [5] | 郭贤烙,钟萍,肖鑫.“四合一”常温钢铁处理液的研究[J].表面技术,2002(03):69-71. |
| [6] | 常青,王健.常温快速磷化工艺的研究[J].表面技术,2003(03):40-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%