研究了在AZ31镁合金表面二次浸锌后直接进行化学镀镍的工艺.分析了pH、温度、镍离子质量浓度和次磷酸钠质量浓度对镀速的影响,并测试了镀层的结合力、表面形貌、成分含量和耐蚀性.结果表明,以二次浸锌法进行预处理,无需氰化镀铜打底;在pH为7,碱式碳酸镍质量浓度25g/L,次磷酸钠质量浓度30g/L时,镀速有最大值;AZ31镁合金化学镀镍后耐蚀性明显提高,腐蚀电位从-1.52 V提高到-0.55 V;化学镀镍的优化参数为15g/L碱式碳酸镍,25g/L次磷酸钠,pH为6,温度82℃.
参考文献
[1] | J.E. Gray;B. Luan .Protective coatings on magnesium and its alloys-a critical review[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):88-113. |
[2] | Hoche H.;Scheerer H.;Probst D.;Broszeit E.;Berger C. .Development of a plasma surface treatment for magnesium alloys to ensure sufficient wear and corrosion resistance[J].Surface & Coatings Technology,2003(0):1018-1023. |
[3] | 郭洪飞,安茂忠.镁及镁合金阳极氧化技术[J].轻合金加工技术,2003(12):1-5,22. |
[4] | CHU L H;CHEN C C;YANG C F .Improvement of corrosion properties in an aluminum-sprayed AZ31 magnesium alloy by a post-hot pressing and anodizing treatment[J].Surface and Coatings Technology,2005,191(2-3):181-187. |
[5] | 刘新宽,向阳辉,王渠东,丁文江.Mg合金的防蚀处理[J].腐蚀科学与防护技术,2001(04):211-213,222. |
[6] | XIANGYH;HU W B;LIU X K et al.A study on surface state during the pretreatment of electroless nickel plating on magnesium alloys[J].Transactions of the Institute of Metal Finishing,2001,79(01):33-34. |
[7] | 李立清,肖友军.镁合金上化学镀镍工艺的研究[J].南方冶金学院学报,2004(05):54-58. |
[8] | 贾志华,王玉平.镁及镁合金化学镀Ni-Cu-P三元合金工艺[J].电镀与涂饰,2004(03):6-8. |
[9] | 李国斌,彭荣华,马淞江.铝基体电镀前浸锌工艺研究[J].电镀与精饰,2003(02):24-26,41. |
[10] | 黄晓梅,李宁,蒋丽敏,黎德育.铝及铝合金电镀的浸锌工艺[J].电镀与环保,2005(02):1-4. |
[11] | 向阳辉,刘新宽,胡文彬,赵昌正,丁文江.镁合金化学镀镍的磷含量控制[J].电镀与环保,2001(02):25-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%