传统镀硬铬技术存在环境污染问题及镀铬层的性能缺陷.综述了几种可以替代镀硬铬的新工艺的特点、性能及其研究现状,包括非晶态合金镀、高速火焰喷涂、镀金刚粉、离子束注入技术等.以上技术有许多优点,但也各有局限性.提出了选择合适镀硬铬替代工艺的要求.
参考文献
[1] | 周克崧,宋进兵,刘敏,代明江,杨大君.热喷涂技术替代电镀硬铬的研究进展[J].材料保护,2002(12):1-4. |
[2] | 佚名.优异代镀铬新工艺-非晶合金镀[J].Anti-corrosion防腐蚀(中文版),2003(09):45. |
[3] | 佚名 .电镀钨基非晶态合金代替镀铬工艺[J].电镀与涂饰,2004,23(06):51. |
[4] | STARTWELL B D.Thermal Spray Coatings as Alternative to Hard Chrome Plating[J].Welding Journal,2000(07):39. |
[5] | KEITH O L.Overview of Chromium and Cadmium Alternative Technologies[A].UK:ASM International,2002 |
[6] | BODER B E;SOMERVILLE D A;EMERY W A et al.The Evaluation of Tungsten Carbide Thermal Spray Coating as Replacements for Electrodeposited Chrome Plating on Aircraft Landing Gear[J].Plating and Surface Finishing,1997,84(09):25. |
[7] | MITCH R D;MONTIA N;ANDREW N.Hard Chromium Coatings Outdated?[J].Sulzer Technical Review,1997(01):20-23. |
[8] | REIGNIER C;STURGEON A;LEE D.HVOF Sprayed WC-Co-Cr as a Generic Coating Type for Replacement of Hard Chrome Plating[A].Essen,Germany:ASM International,2002 |
[9] | KEITH L;BRUCE S.Hard Chrome Alternatives Team Update-Improving Performance While Reduing Cost[A].USA:The American Electroplaters and Surface Finishers Society,2000 |
[10] | SATRWELL B D;NATISHAN P M;SINGER I L.Replacement of Chromium Electroplating Using HVOF Thermal Spray Coatings[A].USA:The American Electroplaters and Surface Finishers Society,1998 |
[11] | ROY MCINTYRE.等离子喷涂与高速氧燃料喷涂工艺的比较[J].国外机车车辆工艺,1997(05):10-12. |
[12] | 晓非.替代镀铬的新工艺-镀金刚粉[J].建材工业信息,1998(09):28. |
[13] | 吴春山.表面处理新工艺-镀金刚粉[J].科技信息(学术版),1999(01):13. |
[14] | 周兴建 .可替代镀铬的离子束技术[J].国外金属热处理,1996,17(05):52-55. |
[15] | 弗朗克N;隆哥.等离子喷涂层-镀铬的替代工艺[J].太重技术导报,1992(03):48-52. |
[16] | SAVARIMUTHU A C;MEGAT I;TABER H F.Sliding Wear Behavior as a Criterion for Replacement of Chromium Electroplate by Tungsten Carbide Thermal Spray Coatings in Aircraft Application[A].Montereal,Canada:ASM International,2000 |
[17] | WASSERMAN C;BOECKING R;GUSTAFSSON S.Replacement of Hard Chrome Plating in Pringting Machniery[A].Ohio,USA:ASM International,2001 |
[18] | ERNING U;NESTLER D C;TAUCHERT G.HVOF Coatings for Hard Chrome Replacement-Properties and Applications[A].Dusseldorf:ASM International,1999 |
[19] | PARKER D S.Case Study:Application of HVOF Sprayed Coatings for Replacement of Chrome Plating on Navy P-3 Aircraft Hydraulic Components and Landing Gear[A].Nice,France:ASM International,1998 |
[20] | NESTLER M C;PRENZEL G;SEITZ T.HVOF Spraying vs.Hard Chrome Plating-coating Characteristics and Aircraft Applications[A].Nice,France:ASM International,1998 |
[21] | RANDOLPH J.HOVOF Facility Qualification at an Airline-Importance and Benefits for Landing Gear Applications[A].Essen,Germany:ASM Thermal Spray Societv,2002 |
[22] | MCGRANN R T R;SHADLEY J R;RYBICK E F.Evaluation of Residual Stresses and Fatigue Life of Tungsten Carbide Thermal Spray Coated Aircraft Landing Gear Materials[C]//[A].Nice,France:ASM International,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%