阐述了机械镀锌层的结构特征,是由金属锌组成的不均连均质体系.锌粉按粒径大小可分为普通锌粉、细锌粉和超细锌粉,按形状可分为球状锌粉、片状锌粉和不规则形状锌粉.分析了锌粉的粒径、颗粒形状、金属锌含量对机械镀锌层的影响.试验得出,超细混合锌粉是机械镀锌工艺较好的选择.
参考文献
| [1] | 刘丽,何明奕.机械镀锌快速活化工艺[J].金属热处理,2000(06):21-23. |
| [2] | BROOKS A .Mechanical plating[J].Metal Finishing,1983,81(08):53-57. |
| [3] | WEINER M .People in finishing:mechanical galvanizers[J].Metal Finishing,1993,91(05):13-14. |
| [4] | ALLISON G M .Mechanical plating[J].Metal Finishing Guidebook,2001,99(1A):399-408. |
| [5] | 何明奕;刘丽;王胜民.机械镀原理及应用[M].北京:机械工业出版社,2003:14. |
| [6] | OSTAPENKO G;KHRAMOVA Y.On mechanism of mechanical zinc plating on steel[A].ESC,2005 |
| [7] | 何明奕,王胜民,刘丽,谭蓉,赵晓军.无结晶金属微粉形成镀层--机械镀[J].金属热处理,2006(02):16-19. |
| [8] | G. Viramontes Ganiboa;M. Medina Noyoia;A. Lopez Valdivieso .The effect of cyanide and lead ions on the cementation rate, stoichiometry and morphology of silver in cementation from cyanide solutions with zinc powder[J].Hydrometallurgy,2005(3/4):193-205. |
| [9] | Gamboa GV;Noyola MM;Valdivieso AL .Fundamental considerations on the mechanisms of silver cementation onto zinc particles in the Merril-Crowe process[J].Journal of Colloid and Interface Science,2005(2):408-414. |
| [10] | GOLBEN M .Process of plating metal objects[P].US 3400012,1968-09-03. |
| [11] | 李铁龙,杨新岐,姜海龙,孙莉.锌粉特性对机械镀锌层性能的影响[J].材料保护,2005(11):14-16. |
| [12] | 徐金富,张亚非,王亮,桂尤国,叶以富.鳞片状超微锌粉制备工艺的研究[J].材料开发与应用,2005(03):28-31. |
| [13] | 单国华.超细鳞片状锌粉的研究[J].有色矿冶,2000(06):40-42. |
| [14] | 陈岁元,刘常升,刘海亚,李会莉.锌铬膜涂料用微细Zn片的制备及研究[J].材料保护,2003(01):39-41. |
| [15] | 蔡晓兰,林兴铭,王国富.用高能球磨制备超细鳞片状锌粉[J].世界有色金属,2004(04):48-49,45. |
| [16] | 宁振立,蔡晓兰.磷片状锌粉的制备工艺研究[J].昆明理工大学学报(理工版),2004(03):33-35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%