为提高低温氯化物电镀铁溶液的稳定性,采用赫尔槽试验和阴极极化曲线测量方法,研究了5种稳定剂对镀层光亮区、阴极极化过程以及镀铁液稳定性的影响.试验结果表明,取抗坏血酸13 mL/L(10%,质量分数,以下同)、氨基酸5 mL/L(10%)、氟化物8 mL/L(10%)组成的复合稳定剂,不仅能显著增大低温氯化物电镀铁镀层光亮区范围,而且当Jk在2～15 A/dm2范围内时,还提高了镀液的阴极极化能力,镀液在敞口的小烧杯中,出现沉淀的时间是305 h.
参考文献
| [1] | Yasushi Ohnishi;Shoji Yoshimoto;Masaki Kato .Metal pattern formation by selective electroless metallization on polypyrrole firms patterned by photochemical degradation of iron(III) chloride as oxidizing agent[J].Synthetic Metals,2004(3):265-269. |
| [2] | 凌家伦.无刻蚀镀铁工艺的应用[J].材料保护,1991(05):36. |
| [3] | 谭玉芳;孙桂香.镀铁技术[M].北京:人民交通出版社,1990 |
| [4] | 李庆伦;于晓中;汪红 等.低温镀铁技术的发展[J].电镀与涂饰,1998,17(04):41-43. |
| [5] | Hirato T.;Yamamoto Y.;Awakura Y. .A new surface modification process of steel by pulse electrolysis with asymmetric alternating potential[J].Surface & Coatings Technology,2003(0):135-138. |
| [6] | 扈心担 .pH值对镀铁层性能及结构的影响[J].材料保护,1997,30(03):10-12. |
| [7] | Kim DJ;Roh YM;Seo MH;Kim JS .Effects of the peak current density and duty cycle on material properties of pulse-plated Ni-P-Fe electrodeposits[J].Surface & Coatings Technology,2005(1):88-93. |
| [8] | 吴勇.低温镀铁质量不稳定的原因及改进措施的探讨[J].望江科技,1993(04):27-30. |
| [9] | 郑华均;毛信表;吕忠良 .稀土添加剂在不对称交直流镀铁中的作用[J].电镀与环保,1998,18(01):8-10. |
| [10] | 陈立佳;康煜平;冯浩然 等.低温直流镀铁液中的添加剂[J].材料保护,1997,30(03):25-27. |
| [11] | 陈立佳;康煜平;洪鹤 .稀土添加剂在镀铁中的应用[J].电镀与涂饰,1997,16(01):41-43. |
| [12] | 康煜平;陈立佳;赵忠俭 .无刻蚀直流镀铁层的组织结构与性能[J].金属热处理,1999,20(03):47-51. |
| [13] | Abd el Meguid EA.;Abe el Rehim SS.;Moustafa EM. .Electroplating of iron from alkaline gluconate baths[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2003(1/2):53-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%