亚稳态的CrNi系奥氏体不锈钢在-196℃拉伸应力应变曲线发现有弹塑性失稳与应力平台现象,试验结果表明应变率增加,εphεL增大.XRD分析证明弹塑性失稳点是应变诱发马氏体形成起始点,应力平台是形变硬化和相变软化在一定应变范围内达到动态平衡造成的,它与吕德斯带在试样中的传播有着本质的不同.测定计算得到:产生单位体积分数马氏体相变所需的应变能,即相变能为3.85×106J/m3,且在弹塑性失稳及应力平台阶段其值保持恒定.
参考文献
| [1] | Zackay V F;Parker E R;Fahr D;Busch R .[J].Transactions ASM,1967,60:252-259. |
| [2] | Olson G B;Cohen M .[J].Metallurgical and Materials Transactions,1975,6A:791-795. |
| [3] | Murr L E;Staudhammer K P;Hecker S S .[J].Metallurgical and Materials Transactions,1982,13A:627-635. |
| [4] | Olson G B;Azrin M .[J].Metallurgical and Materials Transactions,1978,9A(09):713-721. |
| [5] | Suzuki T;Kojima H;Suzuki K et al.[J].Acta Materialia,1977,25:1151-1162. |
| [6] | Mangnon Pat L;Thomas G .[J].Metallurgical and Materials Transactions,1970,1:1577-1594. |
| [7] | Fisher J C;Rogers H C .[J].Acta Materialia,1956,4:180-185. |
| [8] | 哈宽富.金属力学性质的微观理论[M].北京:科学出版社,1983:416. |
| [9] | Hahn G T .[J].Acta Materialia,1962,10:727-738. |
| [10] | Tomota Y;Tanabe K et al.[J].Transactions of the Iron and Steel Institute of Japan,1977,17:159-165. |
| [11] | 唐长国 .西安交通大学[D].北京:中国农业大学,1994. |
| [12] | 周惠久;朱金华;何家文 .[J].西安交通大学学报,1996,30(04):1-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%