在1000至1300C之间测量了六种耐火材料在铁磷模拟核废料熔体和实用硼硅酸盐熔体中的动态腐蚀速度。在铁磷模拟核废料熔体中，致密氧化铝和氧化铬耐火材料有最低的熔线腐蚀速度，二氧化硅、锆英石和AZS耐火材料的腐蚀速度比较高。同时，氧化铝和氧化铬耐火材料在铁磷熔体中的腐蚀速度小于它们在硼硅酸盐熔体DWPF中的腐蚀速度。对氧化铬耐火材料来说，其在三种含有模拟HLW废料的铁磷熔体中的熔线腐蚀速度小于0.1mm/day。可以认为商品化的A1umina和Zircon耐火材料可以用来熔化多种HLW废料，甚至可以熔化含有16%重量百分比Na2O的HLW废料。
参考文献
| [1] | Chen Fuyi;Day D .Dissolution of zircon[J].American Ceramic Society Bulletin,1998,77(04):229-235. |
| [2] | Chen Fuyi Day D .Corrosion of selected refractories bythe iron -phosphate melts[J].British Ceramic Transactions,1999,69:273-278. |
| [3] | Jantzen C;Bibber N;Beam D;Crawford C. PicketedM .Development and characterization of defense wasteprocessing facility (DWPF) environmental assessmentglass standard reference materials[J].British Ceramic Transactions,1994(39):313-322. |
| [4] | KIM D;Hama P;Larmar D;Elliott M .Development ofhigh--waste loaded high level nuclear waste glasses forhigh- temperature melter[J].British Ceramic Transactions,1995,45:39-48. |
| [5] | Rankin W .Advances in Ceramics[Z].Nuclear Waste Management I,1995. |
| [6] | Lifanov F;Stefanovsky S;Kobelev A;Sakin A .Knyazev O , Lashchenova T , Merlin S . Roux P .Vitrification of simulated intermediate-level french andRussian waste in cold crucible based plant[Q]. |
| [7] | Vitrification of simulated intermediate-level french andRussian waste in cold crucible based plant[J].Materials Research Society Symposium Proceedings,1996,4(12):163-171. |
| [8] | Bennert D;Overcamp T;Bickford D;Jantzen C. CiceroC .Demonstration of vitrification of surrogate F006wastewater treatment sludge[J].British Ceramic Transactions,1995,45:73-90. |
| [9] | Marra J C;Overcamp TJ;Erich DL .Melter component performance during surrogate low-level mixedwaste vitrification campaigns[J].Corrosion of Refractoryby Molten Glass Ohio:American Ceramics Society,1996,41:241-251. |
| [10] | Matzke H;Vernaz E .Thermal and physicochemicalproperties important for the long- term behavior ofnuclear waste glass[J].Journal of Nuclear Materials,1993,201:295-309. |
| [11] | Yu XY;Day DE;Long GJ;Brow RK;UNIV MISSOURI DEPT CHEM ROLLA MO 65409.;UNIV MISSOURI GRAD CTR MAT RES ROLLA MO 65409.;SANDIA NATL LABS ALBUQUERQUE NM 87185.;MINIST LIGHT IND PEOPLES REPUBL CHINA GLASS & ENAMEL RES INST SHANGHAI 200052 PEOPLES R CHINA. .Properties and structure of sodium-iron phosphate glasses[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1997(1):21-31. |
| [12] | Cilon G Rouse;Samuel M Toffoli;Alvaro B Lopes.Glass corrosion studies of a high alumina refractory[J].Adv Fusion Glasses,1988:561-568. |
| [13] | Mel'nikova I G;Razdol'skaya IV;Dolivo-Dobrovol'skaya E M;Nesterova T A .Physical andTechnological ProPerties of a Zircon Ceramics, Glassesand Ceramics ( English Translation of Steklo IKeramila)[Z].,1987. |
| [14] | Golovin A I;Pavlovskij V K;Shchavelev O S .Corrosion resistance of ceramics refractories and platinumto lead-phosphates glasses[J].Steklo i Keramika,1992(49):21-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%