基于正交实验设计方法.系统试验研究了氧气流量、燃气流量和喷涂距离对超音速火焰喷涂Cr3C2-NiCr涂层磨粒磨损性能的影响.获得了喷涂工艺条件与涂层磨粒磨损失重量的定量关系和最佳的喷涂工艺参数.并进行了实验验证。结果表明：氧气流量、燃气流量和喷涂距离对涂层磨粒磨损性能具有交互影响。其中燃气流量和氧气流量的影响较为显著.适中的燃气流量和氧气流量有利于获得耐磨性较好的涂层。
参考文献
| [1] | 徐滨士;李长久;工守业;王麟书.热喷涂技术的应用与发展[A].,1997:149-155. |
| [2] | Beczkowiak J;Fischer J;Kellerer H.Advanced carbides and borides for wear resistant coatings properties[A].Kohe:May,1995:1033-1057. |
| [3] | Hwang S Y;Seng B Q.Characterization of build-upresistant plasma sprayed coatings for hearth rolls[A].Kobe:May,1995:59-63. |
| [4] | Sasaki M;Kawakaml F;Komakl C.Characterization ofHVOF sprayed Cr3C2 -NiCr coating[A].Orlando Florida.USA:28may ～5 June,1992:165-170. |
| [5] | 李长久.超音速火焰喷涂条件对Cr3C2NiCr涂层性能的影响[A].,1997:417-422. |
| [6] | Srinibasa Rao D;Sen D;Somaraju K R C.Influence of powder particle velocity and temperature on theproperties of Cr3C2 NiCr coating obtained by detonation-gun[A].NiceFrance,1998:385-393. |
| [7] | Vuoristo P;Niemi K;Makela A.Ahrasion and erosion wear resistance of Cr3C2 - NiCr coatings preparedby detonation and high velocity oxy-fuel spraying[A].Boston.Massachusetts,1994:124-126. |
| [8] | 李长久.碳化钨颗粒尺寸对超音速火焰喷涂WC-Co涂层形成的影响[J].表面工程,1997(02):22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%