进行了Ni+(130keV)、Ti(150keV)离子注入Al2O3(质量分数为85%)-ZrO2(质量分数为15%)陶瓷表面改性试验,对改性陶瓷材料表面进行了X-光衍射谱物相分析、表面导电性分析以及与不锈钢材料的非活性钎焊性能分析.结果表明,注Ni+和注Ti+陶瓷表层导电性未发现明显变化,而注Ti+的陶瓷表层材料在注入剂量达到3×1017ions/cm2时其导电性有明显的提高,这是由于在陶瓷材料表层生成的钛氧化物的导电性较高的原故.离子注入确实可以显著提高陶瓷材料的可焊性,但提高陶瓷材料表面导电性并不是提高其钎焊性能的主要因素.
参考文献
| [1] | Samandi M et al.[J].Nuclear Instruments and Methods in Physics Research,1997,B 127/128:669-672. |
| [2] | Abonneau E;Fuchs G .[J].Journal of Adhesion Science and Technology,1991,5(12):1017-1021. |
| [3] | Shoji Noda.[J].Journal of Meterials Science Letters,1986(05):381-383. |
| [4] | Kossowsky R .[P].ADP001665 |
| [5] | J G Li .[J].Rare Metals,1992,11(01) |
| [6] | Holoe H T et al.Mechanism of ceramic-to-metal adherence: adherence of molybdenum to alumina ceramics[J].Ceramic Age,1954,63(03):3. |
| [7] | 张光华;钟士谦.离子注入技术[M].北京:机械工业出版社,1982 |
| [8] | Farlow G C et al.[J].Nuclear Instruments and Methods in Physics Research,1985,B7/8:541-546. |
| [9] | Appleton B R.[J].Nuclear Instruments and Methods in Physics Research,1984:B167-175. |
| [10] | Nicholas M G.[J].Axtive Metal Brazing |
| [11] | 龚涛 .离子注入结构陶瓷表面改性技术研究[D].兵器工业52研究所 |
| [12] | 崔琳 .离子注入对陶瓷力学性能及摩擦学性能的影响研究[D].峨眉:西南交通大学 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%