分别选择NiCrSiB及其加入不同量Mo元素的NiCrMoSiB(1)、NiCrMoSiB(2)自熔合金粉末和CuNiSiB自熔合金粉末,采用氧乙炔焰粉末喷焊工艺制备覆层,用超声波振动气蚀仪对覆层进行耐气蚀性能研究,用扫描电子显微镜对覆层表面气蚀破坏形貌进行观察.结果表明:含Mo的镍基覆层有较好的耐气蚀性,且随着Mo元素加入量的增加,耐气蚀性增大; CuNiSiB比NiCrSiB覆层耐气蚀能力强.还探讨了覆层气蚀破坏机理.
参考文献
[1] | 段昌国.水轮机沙粒磨损[M].北京:清华大学出版社,1981 |
[2] | 康进兴 .用表面覆层法提高材料耐冲蚀汽蚀性[D].西安交通大学,2001. |
[3] | Kezheng Sang;Yugang Li.Cavitation erosion of flame spray weld coating of nickel-base alloy powder[J].WEAR,1995(189):20-24. |
[4] | GB6383-1986.GB6383-1986.振动空蚀试验方法[S]. |
[5] | Marek Szkodo;Boleslaw G. Giren;Janusz Steller .Cavitation resistance of new chromium-manganese and chromium-cobalt electrodes and their metallographic structures[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(0):111-119. |
[6] | V. A. Pugsley;C. Allen .Microstructure/property relationships in the cavitation erosion of tungsten carbide-cobalt[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(0):93-103. |
[7] | Jiang G B;Zheng Y K;YANG Y Y.Cavition erosion of bainitic steel[J].WEAR,1998(215):46-53. |
[8] | Marcio Gustavo Di Vernieri Cuppari;Frank Wischnowski;Deniol K. Tanaka;Amilton Sinatora .Correlation between microstructure and cavitation-erosion resistance of high-chromium cast steel-preliminary results[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(1):517-522. |
[9] | 孙寿.水泵汽蚀研究的现状[J].水泵技术,1995(03):39-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%