用挤压铸造法制备Al2O3f/Al-4Cu复合材料,研究了冷却速度对复合材料凝固偏析的影响.结果表明,Al-4Cu合金初晶在纤维间隙中生核长大,纤维不能作为α初晶非自发形核衬底;复合材料基体中存在由纤维间隙中心至纤维/基体界面或晶界处渐增的Cu浓度梯度,纤维周围存在共晶第二相偏析;冷却速度增大,凝固偏析加剧;复合材料中由于非平衡结晶生成共晶组织的量可由Clyne-Kurz公式定量计算.
参考文献
| [1] | Li Q F;McCartney D G;Walker A M .Development of solidification microstmctures in a fibre reinforced alloy[J].Journal of Materials Science,1991,26:3565-3574. |
| [2] | Mortensen A;Gungor M N;Cornie J A.Alloy microsegregation in cast metal matrix composites[J].Journal of Metals,1986(03):30-35. |
| [3] | Mortensen A;Cornie J A;Flemings M C.Solidification processing of metal- matrix composites[J].Journal of Metals,1988(02):12-19. |
| [4] | 储双杰;吴人洁.挤压铸造莫来石短纤维增强Al--4.5Cu复合材料的凝固组织、偏析及性能的研究[J].铸造,1998(10):4-7. |
| [5] | 李子全,吴炳尧,沈光俊.不同冷却条件SiCp/ZA-27复合材料界面的TEM观察[J].南京大学学报(自然科学版),2001(01):84-90. |
| [6] | Brody H D;Flemings M C .Solute redistribution in dendritic solidification[J].Transactions of the Metallurgical Society of AIME,1966,236:615-624. |
| [7] | Clyne T W;Kurz M.Solute redistribution during dendritic solidification with rapid solid state diffusion[J].Metallurgical and Materials Transactions,1981(12A):965-971. |
| [8] | 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000:109. |
| [9] | 于思荣;何镇明 .挤压浸渗金属基短纤维复合材料浸渗压的理论分析与应用[J].复合材料学报,1995,12(02):15-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%