研究了微量Sc对Al-3.5Cu-1.5Li-0.12Zr合金微观组织和拉伸性能的影响.结果表明:在Al-3.5Cu-1.5Li-0.12Zr合金中加入0.10%(质量分数)的Sc消除了合金铸态枝晶组织,有效地抑制了再结晶的发生,具有一定的强化作用和明显的增塑效应;添加0.25%(质量分数)的Sc显著细化合金铸态的晶粒组织,促进了合金固溶过程中再结晶的发生,从而降低了合金的强度.
参考文献
| [1] | Kumar K S;Brown S A;Pickens J R .Microstructural evolution during aging of an Al-Li -Mg-Ag-Zr alloys[J].Acta Materialia,1996,44(05):1899-1915. |
| [2] | Lavernia J E;Grant J N .Review aluminium-lithium alloys[J].Journal of Materials Science,1987,22:1521-1529. |
| [3] | Drits A M;Krimova T V.Aluminium-lithium alloys for aerospace[J].Current Advances in Materials and Processes,1998(06):48-51. |
| [4] | Frudljander I N;Kablov E N;Kolobnev N I et al.Aluminumbase alloy and article made of it[P].Russia Patent:2163940,1999-09-08. |
| [5] | Joh C H;Yamada K;Miura Y .Effect of Sc-addition on coarsening behavior of Al3Li precipitates in Al-Li alloys[J].Materials Transactions,1998,5:439-443. |
| [6] | Milman Yu V;Lotsko D V;Sirko O I .Sc effect of improving mechanical properties in aluminum alloys[J].Materials Science Forum,2000,331-337:1107-1112. |
| [7] | TAN Cheng-yu,ZHENG Zi-qiao,XIA Chang-qing.The Aging Feature of Al-Li-Cu-Mg-Zr Alloy Containing Sc[J].中南工业大学学报,2000(02):65. |
| [8] | 夏德顺.含钪的铝和铝锂合金[J].航天工艺,1999(02):37-42. |
| [9] | 杨志强,尹志民.俄罗斯铝-钪合金的研究与开发[J].轻合金加工技术,2003(11):34-36,40. |
| [10] | 潘青林,尹志民,邹景霞,陈显明,张传福.微量Sc在Al-Mg合金中的作用[J].金属学报,2001(07):749-753. |
| [11] | NorMan A F;Prangnell P B;Mcewen R S .The solidification behaviour of dilute aluminum alloys[J].Acta Materialia,1998,16(46):5715-5732. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%