采用包钢CSP薄板坯连铸连轧工艺生产的L245钢为原料进行螺旋焊管焊接生产时,针对生产中焊缝裂纹问题,对焊缝区的形貌、组织进行了观察和晶粒度测定,并对焊缝进行拉伸性能和X射线检验.通过分析L245钢埋弧焊焊缝区质量、微观组织和拉伸性能关系表明,焊接工艺参数的合理制定是低合金钢L245焊管产生裂纹等缺陷的关键因素.
参考文献
| [1] | Belanger R.J.;Patchett B.M. .The Influence of Working Fluid Physical Properties on Weld Qualification for In-Service Pipelines[J].Welding Journal,2000(8):(209-s)-(214-s). |
| [2] | A.P. Cisilino;M.D. Chapetti;J.L. Otegui .Minimum thickness for circumferential sleeve repair fillet welds in corroded gas pipelines[J].International Journal of Pressure Vessels and Piping,2002(1):67-76. |
| [3] | P.N. Sabapathy;M.A. Wahaba .The prediction of burn-through during in-service welding of gas pipelines[J].International Journal of Pressure Vessels and Piping,2000(11):669-677. |
| [4] | 潘家华.我国管材及制管工业的发展趋势[J].焊管,2003(05):1-5. |
| [5] | 王凤英.螺旋焊管生产中的质量控制[J].油气储运,1998(07):50. |
| [6] | 李振亮,陈玉枝,佟铁印.L245钢辊旋焊管成型角优化[J].包头钢铁学院学报,2005(03):288-290. |
| [7] | 李亚江.焊接组织性能与质量控制[M].北京:化学工业出版社,2005 |
| [8] | Yurioka N;Suzuki .Hydrogen assisited cracking in C-Mn and low alloy steel weldments[J].International Materials Reviews,1990,35(04):217. |
| [9] | 王晓香.管线钢焊接常用的几种碳当量公式[J].焊管,2004(02):71-73,76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%