采用料浆烧结法在铌合金C-103基体表面制备Mo(Si0.6,Al0.4)2高温抗氧化涂层,利用SEM、EDS、XRD等仪器分析研究涂层的结构、元素分布、相分布与抗氧化性能的关系.结果表明:涂层与基体之间达到冶金结合,通过扩散形成中间结合层;在高温氧化环境下,Mo(Si0.6,Al0.4)2涂层表面生成致密氧化膜.氧化膜分为两层:外层主要为Al2O3,内层为Al2O3、SiO2、3Al2O3·2SiO2和HfO2相的混合物.
参考文献
| [1] | 冯景苏.铌应用的新进展[J].稀有金属材料与工程,1994(03):7-12. |
| [2] | Tatsuo Tabaru;Kazuhisa Shobu;Hisatoshi Hirai .Influences of Al content and secondary phase of Mo_5(Si,Al)_3 on the oxidation resistance of Al-rich Mo(Si,Al)_2-base composites[J].Intermetallics,2003(7):721-733. |
| [3] | Tabaru T;Shobu K .Oxidation resistance coating for niobium base structure compostes[J].Materials Science Forum,2003,426-432:2581. |
| [4] | P.V. Krakhmalev;E. Strom;C. Li .Microstructure and properties stability of Al-alloyed MoSi_2 matrix composites[J].Intermetallics,2004(2):225-233. |
| [5] | Tabaru T;Shobu K .Effects of substitution of Al for Si on the lattice variations and thermal expansion of Mo (Si,Al)2[J].Intermetallics,2004,12(01):33-41. |
| [6] | Shi Jing.High-temperature oxidation resistant coatings[M].北京:科学出版社,1980:53-55. |
| [7] | 曾燮榕,李贺军,杨峥.碳/碳复合材料表面MoSi2-SiC复相陶瓷涂层及其抗氧化机制[J].硅酸盐学报,1999(01):8-15. |
| [8] | Katsuyuki Yanagihara .Isothermal and cyclic oxidation of Mo (Si1-x,Alx)2 up to 2048K[J].Materials Transactions,1993,34(12):1200-1206. |
| [9] | P.V. Krakhmalev;E. Strom;M. Sundberg .Processing, microstructure and properties of C40 Mo(Si,Al)_2/Al_2O_3 composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):207-213. |
| [10] | Xiao L;Abbaschian R .Interfacial modification in Nb/MoSi2composites and its effects on fracture toughness[J].Materials Science and Engineering,1992,A155:135-145. |
| [11] | Choy K.L.;Balzer R. .Diffusion barrier coatings on ductile particles for protection in bioactive glass-ceramic matrix[J].Journal of the European Ceramic Society,2000(12):2199-2107. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%