用粉末冶金法成功地制备了短碳纤维-镀铜石墨-铜基复合材料,对其体积密度、电阻率、硬度、抗弯强度和摩擦磨损性能进行了测试,观察了它们的显微组织、断口和磨面形貌,并与石墨-铜、镀铜石墨-铜基复合材料进行了对比.结果表明,镀铜碳纤维-镀铜石墨-铜基复合材料的各项性能,明显优于石墨-铜、镀铜石墨-铜基复合材料.
参考文献
| [1] | Eliezer Z .High speed tribological properties of graphite fiber/Cu-Sn matrix composites[J].Wear,1978,49:119-133. |
| [2] | Gan Yongxue;Chen Biankun;Yi Pei.Tribological behavior of carbon fiber reinforced copper matrix composites[A].北京:万国学术出版社,1989:13-16. |
| [3] | 许少凡;王文芳;凤仪 等.碳纤维-中铜-石墨复合材料的摩擦磨损性能研究[J].摩擦学学报,1998,18(03):254-258. |
| [4] | Pavlenko V I;Yas D S .The copper plating of graphite pow ders in the manufacture of copper-graphite materials[J].Porosh Met,1976,2(158):9-13. |
| [5] | Lee P K .High-current brush material development,part Ⅰ,sin tered metal-coated graphite[J].IEEE Transactions on Components Hybrids and Manufacturing Technology,1980,3(01):4-8. |
| [6] | 高强;吴渝英;张国定 等.碳纤维对铜-石墨复合材料性能的影响[J].中国有色金属学报,2000,10:97-101. |
| [7] | 王文芳;许少凡;凤仪 等.用镀铜石墨粉制备铜-石墨复合材料[J].机械工程材料,1999,23(02):41-43. |
| [8] | 王彪,许少凡.石墨表面无敏化及活化的化学镀铜法[J].表面技术,2004(06):55-56. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%