利用热模拟试验机,在温度为1020~1080℃和应变速率为0.001~70 s-1范围内对TC11合金进行真应变为1.2的大应变等温恒应变速率压缩试验,获悉高温塑性流动的应力-应变关系曲线特征,并对变形前后的微观组织进行观察.结果表明:流动应力随应变速率升高和温度降低而增加,但前者比后者对流动应力的影响更为显著;在所研究的温度范围内,当应变速率大于10.0 s-1时,变形组织主要为拉长的β晶粒;当应变速率在1.0~0.01 s-1之间时,变形试样分别发生部分动态再结晶和完全动态再结晶;当应变速率为0.001 s-1时,变形试样以动态回复为主.为获得良好的变形组织,热加工区域以温度在1020~1050℃,应变速率在0.01~1.0 s-1范围为宜.

参考文献

[1] Ding R.;Guo Z.;Wilson A. .Microstructural evolution of a Ti-6Al-4V alloy during thermomechanical processing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(2):233-245.
[2] 王金友;葛志明;周彦邦.航空用钛合金[M].上海:上海科学技术出版社,1985:117.
[3] 李健;周义刚 .TC11钛合金β锻造变形程度及其锻后热处理对组织性能的影响[J].机械工程材料,1998,24(02):22-24.
[4] 周义刚,曾卫东,俞汉清.近β锻造推翻陈旧理论发展了三态组织[J].中国工程科学,2001(05):61-66.
[5] 杨觉先.金属塑性变形物理基础[M].北京:冶金工业出版社,1987:144.
[6] 王敏敏,赵永庆,周廉.Ti40阻燃钛合金的高温蠕变行为[J].稀有金属材料与工程,2003(02):117-120.
[7] 曾卫东.Ti-17合金高温变形机理研究[J].材料工程,1996(09):27.
[8] T. Seshacharyulu;S. C. Medeiros;W. G. Frazier;Y. V. R. K. Prasad .Hot working of commercial Ti-6Al-4V with an equiaxed α-β microstructure: materials modeling considerations[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):184-194.
[9] 冯亮,曲恒磊,赵永庆,李辉,张颖楠,曾卫东.TC21合金的高温变形行为[J].航空材料学报,2004(04):11-13.
[10] 鲍如强,黄旭,黄利军.Ti-10V-2Fe-3Al合金热工艺的研究[J].稀有金属,2005(02):214-218.
[11] Brun M;Anoshkin N;Shakhanova G .Physical processes and regimes of thermomechanical processing controlling development of regulated structure in the α+β titanium alloys[J].Materials Science and Engineering,1998,A243:77-81.
[12] 王占学.塑性加工金属学[M].北京:冶金工业出版社,1989:157.
[13] Seshacharyulu T.;Medeiros SC.;Frazier WG.;Prasad YVRK. .Microstructural mechanisms during hot working of commercial grade Ti-6Al-4V with lamellar starting structure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):112-125.
[14] R. Ding;Z.X. Guo .Microstructural evolution of a Ti-6Al-4V alloy during β-phase processing: experimental and simulative investigations[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):172-179.
[15] Prasad YVRK.;Seshacharyulu T. .Processing maps for hot working of titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):82-88.
[16] T. Seshacharyulu;S. C. Medeiros;J. T. Morgan;J. C. Malas;W. G. Frazier;Y. V. R. K. Prasad .Hot deformation and microstructural damage mechanisms in extra-low interstitial (ELI) grade Ti-6Al-4V[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):289-299.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%