用粉末冶金热压制备了不含石墨以及添加了3%石墨的镍铬萋合金,考察两种合金在900℃时的等温氧化行为,用扫描电镜(SEM)和X射线衍射仪(XRD)分析材料的氧化产物.结果表明,不含石墨时,合金表面氧化生成尖晶石结构的NiCr2O4以及Cr2O3,从而抑制了材料的氧化速度.加入石墨后,由于石墨的氧化分解,在材料表面生成了疏松的Cr2O3,使材料的氧化增重增加.
参考文献
| [1] | 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995:296-305. |
| [2] | Xiang J H;Gesmundo F;Niu Y .The oxidation of two ternary Ni-Cu-10at%Al alloys in 1 atm of pure O2 at 800-900℃[J].Corrosion Science,2004,46:2025-2039. |
| [3] | Ren X;Wang FH;Wang X .High-temperature oxidation and hot corrosion behaviors of the NiCr-CrAl coating on a nickel-based superalloy[J].Surface & Coatings Technology,2005(1/3):425-431. |
| [4] | Z.Q. Cao;Y. Shen;W.H. Liu;Y. Xue .Oxidation of two three-phase Cu-30Ni-Cr alloys at 700-800℃ in 1 atm of pure oxygen[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):138-144. |
| [5] | Rodrguez Morales A;Leon Bravo A;Richter G et al.Influence of oxidation on the hight-temperature mechanical properties of zirconia/nickel cermets[J].Scripta Materialia,2006,54:2087-2090. |
| [6] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:225-235. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%