采用三维形貌及表面粗糙度测量系统研究三维石英纤维增强氮化物基复合材料的烧蚀形貌及表面粗糙度,运用Origin软件对所得形貌及表面粗糙度进行分析.结果表明,氮化物基复合材料在高压高热流等离子体烧蚀下表面粗糙度受烧蚀状态影响明显,随着等离子气流压力和热流密度的提高,表面粗糙度增加.提高材料密度及石英纤维编织件编织均匀性可以降低表面粗糙度并提高材料耐烧蚀性能.
参考文献
| [1] | Donghwan C;Byung Ⅱ Y.Microstructural interpretation of the effect of various matrices on the ablation of carbon-fiber-reinforced composites[J].Composites Science and Technology,2001(61):271-280. |
| [2] | 姜贵庆;刘连元.高速气流传热与烧蚀热防护[M].北京:国防工业出版社,2003:46. |
| [3] | Jiang Y G;Zhang C R;Cao F et al.Fabrication of high performance 2.5D SiO2f/Si3N4-BN composites for high-temperature application[J].Advances in Engineering Materials,2007,9(1-2):1-6. |
| [4] | 石晓斌,王金明,许正辉,杨志翔.多向C/C复合材料烧蚀表面粗糙度初步研究[J].宇航材料工艺,2004(06):24-26,44. |
| [5] | Tanigawa Y;Akai T;Kawamura R et al.Transient heat conduction and thermal stress problems of nonhomogeneous plate with temperature-dependent material properties[J].Journal of the Thermal Stresses,1996,19(01):77-102. |
| [6] | 王俊山,李仲平,敖明,许正辉,刘朗,胡子君,彭维周.掺杂难熔金属碳化物对炭/炭复合材料烧蚀微观结构的影响[J].新型炭材料,2005(02):97-102. |
| [7] | 陈虹,张联盟,李勇,罗文辉,于水,贾光耀.三维编织SiO2基复合材料性能的研究[J].硅酸盐学报,2003(10):918-922. |
| [8] | Miering M B .Thermochemical ablation of ceramic heat shields[J].AIAA Journal,1975,13:610-616. |
| [9] | 史可顺.耐热、介电、结构陶瓷基复合材料的进展[J].特种耐火材料,1982(02):23-27. |
| [10] | 王国雄.弹头技术[M].北京:宇航出版社,1993:9. |
| [11] | 黄志澄;程永鑫.航天空气动力学[M].北京:宇航出版社,1994:328-329. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%