采用Mg基复合变质处理的方法,探讨过共晶高铬铸铁凝固组织的变化特征.研究结果表明,经过Mg基复合变质处理后,铁水的表面张力提高,铁液得到净化,同等冷却条件下,铁液凝固时热力学过冷度增大,不仅使凝固组织中伪共晶程度明显加剧,共晶组织数量有所增加,而且显著改善碳化物形态,从而使高铬铸铁的冲击韧性有较大提高.
参考文献
| [1] | 符寒光.提高低铬铸铁强韧性和抗磨性研究的进展[J].热加工工艺,1995(02):49. |
| [2] | Tabrett C P;Sare I R .The effect of heat treatment on the abrasion resistance of alloy white iron[J].Wear,1997,203-204:206-219. |
| [3] | Hann SK.;Gates JD. .A TRANSFORMATION TOUGHENING WHITE CAST IRON[J].Journal of Materials Science,1997(5):1249-1259. |
| [4] | Powell GLF.;Bee JV. .SECONDARY CARBIDE PRECIPITATION IN AN 18 WT-PERCENT CR-1 WT-PERCENT MO WHITE IRON[J].Journal of Materials Science,1996(3):707-711. |
| [5] | 王兆昌.抗磨白口铸铁的合金化和变质处理的研究[J].北京钢铁学院学报,1982(01):23-31. |
| [6] | Zum Gahr K H.Abrasive wear of white cast iron[J].Wear,1980(64):176-194. |
| [7] | Berza J M.Wear and impact resistant white cast irons[J].The British Foundfryman,1981(10):205-211. |
| [8] | Sare R.Abrasion resistance and fracture toughness of white cast irons[J].Metals and Technology,1979(11):412-419. |
| [9] | 周庆德;饶启昌;苏俊义.铬系白口铸铁的磨损与断裂韧性[A].西安:西安交通大学出版社,1986:1-4. |
| [10] | 马永新;张立珊;段凯禄.高铬铸铁在不同工作条件下磨粒磨损耐磨性的研究[J].北京联合大学学报,1994(03):28-38. |
| [11] | 苏俊义;周庆德.铬系耐磨白口铸铁[M].北京:国防工业出版社,1990:124. |
| [12] | 张承甫;龚建森;黄杏蓉.液态金属的净化与变质[M].上海:上海科学技术出版社,1989:165-222. |
| [13] | 戚正风.固态金属中的扩散与相变[M].北京:机械工业出版社,1998:63-68. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%