在Bao0.55Sr0.45TiO3(BSTO)与质量分数为55%的MgO混合的基础上,进行ZrO2掺杂的系统研究.结果表明.随着ZrO2掺入量的增加,BSTO/MgO材料的损耗基本保持不变,调谐性显著提高,但过量的ZrO2掺杂使得材料的调谐性降低.当ZrO2掺杂1%(摩尔分数)时,BST/MgO材料的介电常数为117,介电损耗为3.95×10-3(3.2 GHz),介电常数调谐性达9.9%(2.0 kV/mm).利用电介质理论分析ZrO2对BST/MgO材料介电性质的改性机理.
参考文献
[1] | 金宇龙,周洪庆,吴洪忠,刘敏,蒋微波,黄志文.钛酸锶钡(BST)铁电移相器材料的研究现状[J].电子元件与材料,2003(02):38-40. |
[2] | Su B;Holmes J E;Meggs C et al.Dielectric and microwave properties of barium strontium titanate(BST)thick films on alumina substrates[J].Journal of the European Ceramic Society,2003,23:2699-2703. |
[3] | Synowczynski J;Sengupta L C;Chiu L H .Investigation of the effect of particle size on the 10 GHz microwave properties of Ba1-x,SrxTiO3/MgO composite ceramics[J].Integrated Ferroelectrics,1998,22:341-352. |
[4] | Y.-C. Chen;C.-L Huang .Dielectric constant tunability of ZrO_2-doped barium strontium titanate for application in phased array antennas[J].Materials Letters,2006(4):451-454. |
[5] | Jih-Wei Liou;Bi-Shiou Chiou .Effect of direct-current biasing on the dielectric propetries of barium strontium titanate[J].Journal of the American Ceramic Society,1997(12):3093-3099. |
[6] | 李标荣;莫以豪.无机介电材料[M].上海:上海科学技术出版社,1986 |
[7] | Zhang L;Hong W L;Wang C L et al.Finite-size effects in ferroelectrie solid solution BaxSr1-xTiO3[J].Journal of Physics D:Applied Physics,1999,32(05):546-551. |
[8] | 杨春霞,周洪庆,刘敏,吴红忠,梁斌斌,金宇龙.BSTO/MgO铁电移相材料的研究[J].电子元件与材料,2005(02):13-15. |
[9] | Sung-Gap Lee;Dae-Seok Kang .Dielectric properties of ZrO_2-doped (Ba,Sr,Ca)TiO_3 ceramics for tunable microwave device applications[J].Materials Letters,2003(9/10):1629-1634. |
[10] | Johnson K M .Variation of dielectric constont with voltage in ferroeleetries and its application to parametric devices[J].Journal of Applied Physics,1962,33(09):2826-2831. |
[11] | 李景德;雷德铭.电介质材料物理和应用[M].广州:中山大学出版社,1992 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%