在不使用粘合剂的情况下,制备3～5μm波段低红外发射率耐高温PbO涂层,研究不同粘结温度条件对涂层发射率的影响,并通过XRD、SEM、IR对样品进行测试.研究结果表明,随着粘结温度的升高、升温速率的减慢及保温时间的延长,涂层样品的发射率都逐渐增大,并从微观结构的角度对样品发射率影响机理给予解释;通过优化工艺条件,可制备发射率最低为0.20的涂层,且制备的涂层比较致密,与基板粘结的非常好.
参考文献
| [1] | Zueco, J;Alhama, F .Inverse estimation of temperature dependent emissivity of solid metals[J].Journal of Quantitative Spectroscopy & Radiative Transfer,2006(1):73-86. |
| [2] | Kou W;Yang L.Error analysis of temperature measurement using infrared thermography for navalship[J].Energy Conversion and Application,2001(02):1301-1304. |
| [3] | Supcoe R F;Greenberg M .Dark coating with low solar infrared absobing properties[P].US 5749959,1998-05-12. |
| [4] | 张卫东,冯小云,孟秀兰.国外隐身材料研究进展[J].宇航材料工艺,2000(03):1-4,10. |
| [5] | 胡传炘.隐身涂层技术[M].北京:化学工业出版社,2004 |
| [6] | Lews C F .Materials keep a low profile[J].Materials and Engineering,1988,6(03):37. |
| [7] | XIE Guohua,ZHANG Zuoguang,WU Ruibin.Matching Performance among Visible and near Infrared Coating, Low Infrared Emitting Coating and Microwave Absorbing Coating[J].武汉理工大学学报（材料科学版）英,2005(04):55-59. |
| [8] | 白学福,梁永辉,江文杰.红外搜索跟踪系统的关键技术和发展前景[J].国防科技,2007(01):34-36. |
| [9] | 吴剑锋,何广军,赵玉芹.飞机尾向的红外辐射特性计算[J].空军工程大学学报（自然科学版）,2006(06):26-28. |
| [10] | 夏德宏,余涛,吴祥宇,张省现.热辐射波在介质内的散射机理[J].北京科技大学学报,2006(02):175-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%