选用GCr15轴承钢为基体,WC颗粒为增强相,采用离心铸造工艺制备WC/钢复合材料-LGJW20.用金相分析、电镜扫描(SEM)、X射线衍射(XRD)及能谱分析(EDS)等方法研究材料铸态的相变过程及显微组织.研究结果表明:LGJW20显微组织中基体主要为细小的珠光体组织,基体中析出大量M_(23)C_6及MC型等细小碳化物颗粒;WC原始颗粒以各种复式碳化物的形式析出,分别形成枝状或鱼骨状共晶碳化物、网状二次碳化物及大块状碳化物.
The WC/steel matrix composite LGJW20 was prepared by centrifugal casting with bearing steel GCr15 as matrix material and WC particles as hard phase.The process of phase transformation and microstructure of as-cast composite were investigated by using OM,SEM,XRD and EDS.The results show that the matrix in LCJW20 microstructure is pearlite,a large number of fine carbide particles such as M_(23)C_6 and MC are precipitated in the steel matrix.Multiple carbides are precipitated from WC particles,which form many different shapes such as dendrite or fishbone eutectic carbide,reticulation secondary carbide and conglomeration carbide.
参考文献
| [1] | 冯培忠,强颖怀,王晓虹.离心铸造颗粒增强金属基复合材料的硬度行为[J].金属热处理,2004(07):28-31. |
| [2] | 丁向东,刘刚,王瑞红,孙军,江中浩,连建设.颗粒增强金属基复合材料的屈服行为[J].金属学报,2002(04):369-375. |
| [3] | 湛永钟,张国定,蔡宏伟.颗粒增强金属基复合材料的干摩擦性能与磨损机理[J].材料科学与工程学报,2003(05):748-752. |
| [4] | 杨涛林,陈跃.颗粒增强金属基复合材料的研究进展[J].铸造技术,2006(08):871-873. |
| [5] | 李进,杨智春.SiCp/Al复合材料抗弯性能的试验研究[J].兵器材料科学与工程,2008(06):68-70. |
| [6] | 陈雷,毛昌辉,杨剑,梁秋实.（W+CeO2）p/2024Al复合材料锻造性能研究[J].兵器材料科学与工程,2008(06):24-27. |
| [7] | 孔令超,宋卫东,宁建国,毛小南.增强相形态对金属基复合材料力学性能的影响[J].有色金属（冶炼部分）,2008(06):34-37. |
| [8] | 董小磊,高国富,马星辉.颗粒增强金属基复合材料加工表面质量的研究[J].工具技术,2008(12):22-25. |
| [9] | 李德溥,姚英学,袁哲俊.颗粒增强金属基复合材料加工技术进展[J].工具技术,2006(10):3-9. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%