采用挤压铸造制备Mg-Nd-Gd-Zr镁合金试样.对该合金分组T6热处理后发现,固溶温度由510℃增至540℃过程中,抗拉强度呈先升后降趋势,伸长率持续下降.530℃固溶温度下同溶时间由8 h延长至20 h,合金晶粒长大明显,但伸长率增加100%.SEM分析表明,不同温度同溶处理后合金拉伸断口有区别,510℃固溶处理后断口由残留相开裂和穿晶解理开裂面构成,530℃固溶处理后断口以准解理穿晶断裂为主.

Mg-Nd-Gd-Zr alloy was prepared by squeeze casting.The effect of solution temperature and solution time of heat treatment on the property of the alloy Was studied.The results show that.with the solution temperature increasing from 510℃ to 540℃,the ultimate tensile strength(UTS)increased firstly and then decreased,and the elongation rate reduced continuously.When the solution time Was prolonged from 8 h to 20 h,the grain grew up obviously,while the elongation rate increased by 100%.SEM scanning analysis of the fracture surface shows that,after heat treatment at 510℃,the fracture surface of experimental alloy was made up of cracked section of the retained phase and transcrystalline fracture,while at 530 ℃,quasi-cleavage fracture is the main feature.

参考文献

[1] Friedrich Hoist E;Mordike Barry L.Magnesium technology[M].Springer-Verlag Berlin Herdelberg,2006:212.
[2] 丁文江.镁合金科学与技术[M].北京:科学出版社,2007:100-101.
[3] 李杰华,介万奇,杨光昱.稀土Gd对Mg-Nd-Zn-Zr镁合金组织和性能的影响[J].稀有金属材料与工程,2008(10):1751-1755.
[4] 蒋海燕;付彭怀;彭立明.Mg-3Nd-0.2Zn-0.4Zr合金的显微组织与力学性能[J].特种铸造及有色合金,2008(年会专刊):254-258.
[5] 马志新,李德富,李彦利.Mg-Y-Nd-Zr合金加工工艺与组织演化的研究[J].稀有金属,2006(06):719-723.
[6] 夏长清,武文花,吴安如,王银娜.Mg-Nd-Zn-Zr稀土镁合金的热变形行为[J].中国有色金属学报,2004(11):1810-1816.
[7] LI Jie-hua,JIE Wan-qi,YANG Guang-yu.Effect of gadolinium on aged hardening behavior, microstructure and mechanical properties of Mg-Nd-Zn-Zr alloy[J].中国有色金属学会会刊(英文版),2008(z1):27-32.
[8] 余琨,黎文献,张世军.铸造Mg-RE-Zn-Zr合金的组织和性能[J].特种铸造及有色合金,2001(06):6-8.
[9] G. Ben-Hamu;D. Eliezer;K.S. Shi .The relation between microstructure and corrosion behavior of Mg-Y-RE-Zr alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):269-276.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%