采用氧乙炔火焰喷涂技术,在镁合金AZ31B表面制备Al2O3纳米陶瓷涂层.采用X射线衍射(XRD)、扫描电镜(SEM)分析复合陶瓷涂层的组成及组织形貌,并对其热震性能、致密性、耐磨性和耐蚀性进行测试.结果表明,热喷涂纳米陶瓷涂层中有AlTi3、Al2TiO5等新相生成,组织更为致密,颗粒熔化程度较高,涂层热震性能、致密性、耐磨性和耐蚀性明显优于热喷涂微米陶瓷涂层.热喷涂纳米陶瓷涂层热震次数可达40次,说明涂层结合强度较高,清漆封孔后,孔隙率为0,致密性和耐蚀性都达到最好.
参考文献
| [1] | 侯根良,王汉功,杨晖,苏勋家.冷喷涂技术制备纳米涂层[J].兵器材料科学与工程,2003(02):49-51. |
| [2] | Cell M;Jordan E H;Sohn Y H.Development and implementation of plasmas prayed nanostructured ceramic coatings[J].Surface and Coatings Technology,2001(146/147):48-54. |
| [3] | Song EP;Ahn J;Lee S;Kim NJ .Microstructure and wear resistance of nanostructured Al2O3-8wt.%TiO2 coatings plasma-sprayed with nanopowders[J].Surface & Coatings Technology,2006(3/4):1309-1315. |
| [4] | 魏璐,李京龙,李贺军.热喷涂纳米结构涂层的研究[J].焊接,2007(03):18-23. |
| [5] | 周立忠,阎殿然,何继宁,李香芝.热喷涂纳米陶瓷涂层的制备及性能[J].材料导报,2004(z1):42-44,48. |
| [6] | Goberman D;Sohn Y H;Shaw L et al.Microstructure development of Al2O3-13wt.%TiO2 plasma sprayed coatings derived from nanocrystalline powders[J].Acta Materials,2002,50:1141-1152. |
| [7] | Luo H.;Goberman D.;Shaw L.;Gell M. .Indentation fracture behavior of plasma-sprayed nanostructured Al2O3-13wt.%TiO2 coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):237-245. |
| [8] | 唐红艳,王继辉,肖永栋,张毅.一种新型无机耐烧蚀复合材料固化机理的研究[J].宇航材料工艺,2005(04):25-28. |
| [9] | 李广海;江安全;张立德 .添加纳米Al2O3陶瓷增韧和增强的影响[J].金属学报,1996,32(12):1286-1288. |
| [10] | 时海芳,吕文涛,马壮,李智超.镁合金表面纳米Al2O3基陶瓷涂层的制备及其性能研究[J].材料保护,2008(08):49-51. |
| [11] | 何臣,侯书恩.纳米材料在纳米热喷涂中的应用[J].湖北汽车工业学院学报,2005(01):27-29. |
| [12] | Kear B H;Strutt P R.Chemical processing and application of nanostructured materials[J].Nanostructured Materials,1995(06):227-236. |
| [13] | 刘润,赵剑峰,黄因慧,花国然.纳米复合陶瓷涂层激光熔覆后的组织与耐磨性能[J].中国表面工程,2003(05):39-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%