采用改进的电弧喷涂工艺在钢基底上制备WC颗粒增强钢基复合涂层,并对其进行钨极氩弧重熔以获得与基材呈冶金结合的耐磨复合涂层.利用光学显微镜、SEM、XRD、显微硬度计对涂层成分、组织、相结构及显微硬度进行测试.结果表明:电弧喷涂WC-钢基复合涂层经钨极氩弧重熔后,涂层的致密度提高,组织细小均匀,熔覆层与基材形成良好的冶金结合,熔覆层由F、P和其上分布的均匀、细小WC颗粒组成,无二次析出相,涂层的组织较之重熔前显著改善.
参考文献
[1] | Yandouzi M;Jodoin B.WC-based coating production by the pulsed gas dynamic spraying process:Coatings and process analysis[A].,2009:219-224. |
[2] | M. R. Thakare;J. A. Wharton;R. J. K. Wood;C. Menger .Investigation of micro-scale abrasion-corrosion of WC-based sintered hardmetal and sprayed coating using in situ electrochemical current-noise measurements[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2009(11):1967-1977. |
[3] | M.P. Planche;H. Liao;G. Montavon;C. Coddet .CHARACTERIZATION OF THE WIRE ARC SPRAY PROCESS VIA IMAGE ANALYSIS, IN-FLIGHT PARTICLE CHARACTERISTICS AND COATING PROPERTIES[J].High Temperature Material Processes,2009(1):1-23. |
[4] | Yoshimasa Noda;Akira Sato;Shogo Tobe .Development of Alternative Method of Blasting and Ultra-High Adhesive Strength Thermal Spray Coatings by Vacuum Arc Treatment[J].Materials transactions,2009(4):825-831. |
[5] | Richard Luding;Richard Thorpe;Ryan V. Hinckley .The Development of Twin Wire Arc and HP/HVOF Sprayed Coatings for Coal-Fired Steam Generation Boiler[J].Advanced Materials & Processes,2010(2):34-36. |
[6] | Van Rodljnen F;Knapp S;Wilden J.Production of particle reinforced graded coatings by wire arc spraying[A].,2009:648-652. |
[7] | W. Tillmann;E. Vogli;M. Abdulgader;M. Gurris;D. Kuzmin;S. Turek .Particle Behavior During the Arc Spraying Process with Cored Wires[J].Journal of Thermal Spray Technology,2008(5/6):966-973. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%