分析以往钛/钢复合板爆炸焊接装药量计算过程中存在的问题,结合可焊性窗口下限理论及爆速试验结果,提出钛/钢复合板爆炸焊接装药厚度下限的计算方法,从数值上阐明装药厚度下限值与复板厚度、复板密度、炸药参数、基复板最小碰撞速度之间的函数关系.参照此装药厚度下限值进行钛/钢复合板爆炸焊接验证试验,结果表明,钛金属复板的延展变形得到很好的控制,结合界面没有产生Ti-Fe脆性金属间化合物,结合界面抗剪切强度达到380 MPa.
参考文献
| [1] | 韩丽青,王自东,林国标,张鸿,李锋.爆炸复合TA2/316L板的组织和性能研究[J].材料热处理学报,2008(01):107-110. |
| [2] | 刘鹏,陆明,田涛,余龙.钛/钢复合板爆炸焊接试验及结合界面研究[J].热加工工艺,2010(07):30-33. |
| [3] | 冯健,史和庆.钛/钢复合板爆炸焊接后周边端部被撕裂的机理分析[J].压力容器,2008(02):1-4. |
| [4] | 郑远谋.爆炸焊接和金属复合材料及其工程应用[M].长沙:中南大学出版社,2002:193-194. |
| [5] | Yoshikazu H;Kenji M;Yukio K.Detonation characteristics of emulsion explosive as functions of void and volumo[A].,2002:149-157. |
| [6] | Yoshida M;Lida M;Tanaka K.Detonation behavior of emulsion explosives containing glass microballoons[A].,1985:993-1000. |
| [7] | Lee J;Persson P-A .Detonation behavior of emulsion explosives[J].Propellants,Explosives,Pyrotechnics,1990,15(05):208-216. |
| [8] | Chaudhri M M;Almgren L A;Persson A.Detonation behavior of water-in-oil type emulsion explosive containing glass micro-baloons of selected sizes[A].,1993:741-748. |
| [9] | 宋锦泉 .乳化炸药爆轰特性研究[D].北京科技大学,2000. |
| [10] | 陆明,王耀华,尤峻,刘鹏.爆炸焊接可焊性窗口下限药量试验研究[J].焊接学报,2002(06):44-46. |
| [11] | Lu M;Liu P;Li L.Research on the motion model of flying plate in explosive welding[J].Current Advancements in Molecular Medicines,2010(108/111):1152-1157. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%