论述了国内外汽车用合金化热镀锌钢板的发展趋向.简要介绍了合金化热镀锌IF钢的传统强化方法和新强化技术的应用,并指出该钢种主要是在保证优良成型性能的前提下逐渐向高强化方向发展;详细介绍了340 MPa级别合金化热镀锌烘烤硬化钢的开发情况,指出该钢种主要向易成型、抗粉化和抗时效方向发展;简要介绍了合金化热镀锌低碳当量型高强钢和双相钢的开发进展情况,指出该钢种主要向易成型方向发展.还简述了目前合金化热镀锌TRIP钢的开发进展情况,并指出我国应大力发展汽车用合金化热镀锌钢板,特别是高强度级别的合金化热镀锌钢板,以满足我国飞速发展的汽车工业需求.
参考文献
[1] | Moon Hi HONG;Takeharu KATO;Hiroyasu SAKA .Identification of the Fe-Zn Intermetallic Phases by TEM[J].Tetsu To Hagane-Journal of The Iron and Steel Institute of Japan,1997,83(05):25-30. |
[2] | Masayuki HANMYO .Production and Technology of Iron and Steel in Japan during 2000[J].ISIJ International,2001(7):665-669. |
[3] | Kazuaki Kyono;Tetsuo Shimizu;Kei Sakata.Development of High Strength Grade Galvannealed Sheet Steels[A].:121-128. |
[4] | Hon-Bor Chen;Kang-Ming Hsu.Improvement of the Powdering Resistance of 340H Bake-Hardening GA Sheet Steel[A].:559-564. |
[5] | Kazunori Osawa;Yoshitsugu Suzuki;Shungo Tanaka .TS590 approx 980 MPa Grade Low-Carbon Equivalent Type Galvannealed Sheet Steels with Superior Spot-Weldability[J].Kawasaki Steel Technical Report,2003(48):9-16. |
[6] | Takashi Iwama;FusatoKitano;Yasunobu Nagataki.Development of Galvannealed Dual-Phase Ultra-High Strength Steel Sheets with Superior Formability and Spot-Weldability[A].:539-545. |
[7] | Maki J;MahieuJ;Claessens S.Hot Dip Galvanising of Si-free CMnAl TRIP Steels[A].:623-630. |
[8] | Mintz B .Review on the Hot Dip Galvanisability of Low Si TRIP and Dual Phase Steels with 590 Mpa Strengths[Z].Galvatech',2001. |
[9] | J. MAHIEU;S. CLAESSENS;B. C. De COOMAN .Galvanizability of High-Strength Steels for Automotive Applications[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(11):2905-2908. |
[10] | J. Mahieu;B.C. De Cooman;J. Maki .Hot-Dip Galvanizing of Al Alloyed TRIP Steels[J].Iron & Steelmaker,2002(6):29-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%