采用膨胀法测定了攀枝花新钢钒热轧板厂的高强度P510L钒微合金化钢的CCT曲线,采用金相显微镜分析不同冷速下的显微组织.分析发现,冷却速度较慢(低于10℃/s)时,得到的显微组织为比较粗大的铁素体+珠光体组织;中速冷却时,组织为比较细小均匀的铁素体+珠光体组织;快冷时(高于35℃/s)主要为贝氏体和铁素体组织.进一步采用扫描电镜分析P510L显微组织,发现大量钒的析出物,V(CN)析出物的形态为从球形至长方形,其大小为10～30 nm.
参考文献
| [1] | Crowther D N;Li Y;Baker T N;Green M J W, Mitchell P S.The Development of Vanadium Containing High Strength Steels for Thin Slab Casting[A].London:The Institute of Materials,2000:527-536. |
| [2] | Hawbolt E B;Chau B;Brimacombe J K .Kinetics of Austenite-ferrite and Austenite-pearlite Transformations in a 1025 Carbon Steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16A:565-578. |
| [3] | Kumar A;Mc Culloch C;Hawbolt E B;Samarasekera I V.Modelling Thermal and Microstructural Evolution on Runout Table of Hot Strip Mill[J].Materials Science and Technology,1991(07):360-367. |
| [4] | Devadas C;Samarasekera I V;Hawbolt E B .The Thermal and Metallurgical State of Steel Strip during Hot Rolling:Part Ⅲ Microstructural Evolution[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22A:335-349. |
| [5] | 小指军夫;李伏桃;陈岿.控制轧制与控制冷却[M].北京:冶金工业出版社,2002:85. |
| [6] | Sellars C M .Computer Modelling of Hot-Working Processes[J].Materials Science and Technology,1985,14(01):325-332. |
| [7] | 林惠国;傅代直.钢的奥氏体转变曲线-原理、测试与应用[M].北京:机械工业出版社,1988:110-125. |
| [8] | 李曼云;孙本荣.钢的控制轧制和控制冷却技术手册[M].北京:冶金工业出版社,1998:180-189. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%