利用交流微弧氧化方法在NaAlO2溶液中在Ti-6Al-4V合金表面制备出氧化物陶瓷膜,用扫描电镜及能谱仪研究了陶瓷膜的形貌、组织和Ti、Al、O元素的分布,并用X射线衍射分析了陶瓷膜的相组成. 所制备的陶瓷膜与基体界面结合良好,膜厚约50微米,分为内外两层. 外层膜由大量TiAl2O5相及少量金红石型TiO2相组成. 内层膜的TiAl2O5相含量显著降低,金红石则成为主体相,同时还发现少量TiO1.9相. 这些相都是由微弧区熔融物快速冷却形成的. 微弧区高温高压过程没有改变膜/基体界面附近的合金基体组织.
参考文献
| [1] | ALADJEM A.Review: Anodic oxidation of titanium and its alloy s[J].Journal of Materials Science,1973(08):688-704. |
| [2] | 何文芳 .钛阳极氧化[J].电镀与环保,1998,18(06):26-27. |
| [3] | MALYSCHEV V .Mikrolichtbogen oxidation[J].Metallober flache,1995,49(08):606-608. |
| [4] | МАЛЫШЕВВН;СОРОКИНГМ .КРИТЕРИЙИЗНАШИВАНИЯПОКРЫТИЙ,СФОРМИРОВ-АННЫХМИКРОДУГОВЫММЕТОДОМ[J].ТРЕНИЕИИЗНОС,1996,17(05):653-656. |
| [5] | Xue WB.;Lai YC.;Chen RY.;Deng ZW. .Analysis of phase distribution for ceramic coatings formed by microarc oxidation on aluminum alloy[J].Journal of the American Ceramic Society,1998(5):1365-1368. |
| [6] | 薛文斌,邓志威,张通和,陈如意,李永良.铸造镁合金微弧氧化机理[J].稀有金属材料与工程,1999(06):353-356. |
| [7] | 薛文斌;邓志威;陈如意 等.微弧氧化表面处理对铝合金拉伸性能的影响[J].金属热处理学报,1999,20(04):1-5. |
| [8] | 薛文斌;来永春;邓志威 等.LY12铝合金微等离子体氧化陶瓷膜的相分布及显微硬度分析[J].材料科学与工艺,1999,7(02):18-21. |
| [9] | 薛文斌;邓志威;陈如意 等.铝合金微弧氧化膜与基体界面区的硬度和弹性模量分布[J].金属学报,1999,35(06):638-642. |
| [10] | ГОРДИЕНКОПС;ГНЕДЕНКОВСВ;ХРИСАНФОВАОА, Нgp.ПОВЕДЕНИЕВМОРСКОйВОДЕПОКРЫТИйНАТИТАНЕ,СФОРМИРОВАННЫХМЕТОДОММИКРОДУГОВОГООКСИДИРОВАНИЯВЭЛЕКТ -РОЛИТАХРАЗЛИЧНОГОСОСТАВАБ[J].ФИЗХИМОБРАБМАТЕР,1995(03):77-83. |
| [11] | SCHRECKENBACH J;SCHLOTTIG F;MMARX G.Preparati on and microstructure characterization of anodic spark deposited barium titanate films[J].Journal of Materials Research,1999(13):1437-1443. |
| [12] | KLAPKIV M D .State of an electrolytic plasma in the process of synthesis of oxides based on Aluminum[J].Materials Science,1995,31(04):494-499. |
| [13] | MURRAY J L;WRIEDT H A .The O-Ti(Oxygen-Titanium) system[J].Bulletin Alloy Phase Diagrams,1987,8(02):148-165. |
| [14] | FISCHER E .Thermodynamic Calculation of the O-Ti System[J].Journal of Phase Equilibria,1997,18(04):338-343. |
| [15] | LEE B J;SAUNDERS N .Thermodynamic evaluation of the Ti-Al- O ternary system[J].Zeitschrift fur Metallkunde,1997,88(02):152-161. |
| [16] | 邱关明;黄良钊.玻璃形成学[M].北京:兵器工业出版社,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%