为提高铸铁表面大面积激光熔敷层抗裂性问题,通过冶金因元素控制熔敷层组织形态在熔敷材料中加入碱金属元素钾,研究了在激光快速加热条件下钾对铸铁激光熔敷层组织团球化的影响,进而分析了该球状组织对熔敷层抗裂性的影响.结果表明随熔敷金属内钾含量增多熔敷层内共晶碳化物组织呈球状及孤岛状,这种组织明显提高了熔敷层抗裂性;此外大量的渗碳体组织确保了熔敷层具有较高的耐磨性.获得了无裂纹的大面积搭接熔敷层.其对应合金系统为Fe-C-Si-Ni-K.
参考文献
| [1] | 韩培德;武晓雷 .铁基合金激光熔敷组织及其冲击磨损性能[J].材料科学与工艺,1999,7(02):22-26. |
| [2] | HUJD;LUAN J F;ZHOU Z F .Wear resistance of austenits-TiC-graphite microstructures prepared by laser coating[J].材料科学与工艺(英文版),2001,17(05):558-592. |
| [3] | Jingfei Luan;Jiandong Hu;Zhenfeng Zhou .Microstructure and wear resistance of ductile cast iron laser clad with Ni-Ti-Co-C[J].Journal of Materials Science & Technology,1999(3):222-224. |
| [4] | MEI J;XIAO P.Evaluating degradation of thermal barrier coatings non-destructively using A. C. impedance spectroscopy[A].Indianapolish:[s,n],1999:213. |
| [5] | Steen W M.The Industrial Laser Annual Handbook[M].Tulsa:Penn Well Publ,1987 |
| [6] | 栾景飞,胡建东,周振丰,孙大谦,郭作兴,王红颍.激光熔覆参数对灰铸铁激光熔覆层裂纹的影响[J].应用激光,2000(02):53-56,60. |
| [7] | M. Qian;W. Zhaochang;S. Harada .Initiation and propagation of microcracks in white cast irons under static indentation test[J].Transactions of the American Foundrymen's Society,1996(104):729-733. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%