利用盘销摩擦磨损试验机,分别研究了氧化铜和硅灰石两种无机填料对双马来酰亚胺与硬铝合金的滑动摩擦磨损性能的影响.结果表明:两种填料加入都可以改善双马来酰亚胺的摩擦学性能,随氧化铜用量增加,滑动副的摩擦系数和耐磨性均增加;随硅灰石用量增加和粒径减小,滑动副的耐磨性提高,摩擦系数减小.扫描电镜的分析表明,硅灰石和氧化铜提高滑动副耐磨性的原因是它们促进了双马来酰亚胺在铝环表面形成牢固的转移膜.
参考文献
[1] | K Friedrich .Sliding wear performance of different polyimide formulations[J].Tribology International,1989,22:25-31. |
[2] | S Bahadur;D.Gong .The role of copper compounds as fillers in the transfer and wear behavior of PEEK[J].Wear,1992,154:151-165. |
[3] | Jaydeep Khedkar;Ioan Negulescu;Efstathios I. Meletis .Sliding wear behavior of PTFE composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2002(5/6):361-369. |
[4] | 黄丽,徐定宇,程红原.改性聚酰亚胺摩擦磨损性能的研究[J].复合材料学报,1999(01):63-66. |
[5] | S.Bahadur;D.Gong .The action of fillers in the modification of the tribological behavior of polymers[J].,1992,158:41-59. |
[6] | 曲建俊;李晓光;张志谦 .硅线石颗粒填充双马来酰亚胺摩擦学性能研究[J].材料科学与工艺,1998,7(02):65-68. |
[7] | 曲建俊.硅灰石粉填充丁腈橡胶摩擦磨损性能研究[J].机械工程师,1997(03):8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%