常规TIG焊生产效率低,单道焊可焊厚度小.活性化TIG焊(A-TIG),同常规TIG焊相比可大幅度地提高焊缝熔深,从而提高焊接效率.针对不锈钢材料,通过宏观断面分析方法研究了单一成分的活性剂(SiO2、CaF2、TiO2、Cr2O3和NaF)对焊缝熔深的影响.结果表明:同常规TIG焊相比,上述5种活性剂在涂敷量较小时,焊缝熔深均随活性剂涂敷量的增加而明显增大,氧化物活性剂增加熔深的作用效果大,氟化物的作用效果较小;5种活性剂在熔深增加能力上均有一个饱和点;电弧收缩和熔池表面张力梯度的变化是活性剂增加熔深的主要原因.
参考文献
| [1] | P.J.Modenesi;I.M.Pereira .TIG welding with single-component fluxes[J].Journal of Materials Processing Technology,2000(s1-3):260-265. |
| [2] | Paton B E .The weldability steels that have been refinedby remelting[J].Automatic Welding,1974,27(06):1-4. |
| [3] | Howse D.;Lucas W. .Activating flux-increasing the performance and productivity of the TIG and plasma processes[J].Welding & Metal Fabrication: Welding and Joining Practice and Technology,1996(1):11-17. |
| [4] | PASKELL T;LUNDIN C.GTAW flux increases weld joint penetration[J].Welding Journal,1997(04):57-62. |
| [5] | Takeuchi Y;TAKAGI R;SHINODA T .Effect of bismuth on weld joint penetration in austenitic stainless steel[J].Welding Journal,1992,71(08):283S-289S. |
| [6] | 林三宝,杨春利,刘凤尧,吴林.不锈钢TIG焊活性剂对焊缝性能的影响[J].哈尔滨工业大学学报,2002(03):308-311. |
| [7] | 刘凤尧,林三宝,杨春利,吴林.TIG焊活性剂对焊缝成形的影响[J].焊接学报,2002(01):1-4. |
| [8] | 刘凤尧,林三宝,杨春利,吴林.活性化TIG焊中活性剂和焊接参数对焊缝深宽比的影响[J].焊接学报,2002(02):5-8. |
| [9] | METCALF J C;QUIGLEY M B .Arc and pool instability in GTA welding[J].Welding Journal,1968,47(05):133-139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%