以ZnSO4、(NH4)2S为原料,通过加入分散剂对传统的液相沉淀法进行改进,制备出ZnS的纳米粉末,并探讨了制备过程中沉淀、洗涤、干燥以及晶化等阶段的反应条件对产物的影响.结果表明:以丙三醇为分散剂、原料配比(n(ZnSO4)/n((NH4)2S)为1∶0.9、料液浓度比1∶1,c(ZnSO4)、c((NH4)2 S)均为0.2 mol/L时为沉淀适宜工艺条件;干燥前对沉淀物用无水乙醇进行脱水处理,可有效地控制硬团聚体的产生;沉淀经400～600 ℃晶化1 h, 可得立方晶形β-ZnS纳米晶,产物为均匀球形,分散性较好;400 ℃晶化的产物晶粒尺寸约为40 nm;600 ℃晶化的产物晶粒尺寸约为50 nm.
参考文献
| [1] | CARDON M;HARBEKE G .Optical properties and band structure of wurtzite-type crystals and rutile[J].Physical Review A,1965,137:1467-1476. |
| [2] | 杨桦;王子忱;赵纯 等.掺杂锰的硫化锌纳米晶的光学性质[J].材料研究学报,1996,10(05):544-546. |
| [3] | Bhargava R N;GALLAGHER D;WELKER T .Doped nanocrystals of semiconductors-a new class of luminescent materials[J].Journal of Luminescence,1994,60-61:275-280. |
| [4] | Wada Yuji;YIN Hengbo;KITAMURA Takayuki.Photoductive dechlorination of chlorinated benzene derivatives catalyzed by ZnS nanocrystallites[J].Chemical Communications,1998(24):2683-2684. |
| [5] | Daisuke Adachi;Shigeki Hasui;Toshihiko Toyama .Structural and luminescence properties of nanostructured ZnS:Mn[J].Applied physics letters,2000(9):1301-1303. |
| [6] | 李义和,王本根,傅圣利,王清华.掺杂ZnS半导体纳米微晶材料的研究进展[J].化学研究与应用,2000(01):5-8. |
| [7] | Yang P.;Xu D.;Yuan DL.;Zhou GJ.;Lu MK. .ZnS nanocrystals co-activated by transition metals and rare-earth metals - a new class of luminescent materials[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,2001(2):101-105. |
| [8] | 黄宵滨;马季铭;程虎民 等.乳状液法制备ZnS纳米粒子[J].应用化学,1997,14(01):117-118. |
| [9] | 苏宜;谢宜;陈乾旺 等.纳米ZnS、CdS水热合成及表征[J].应用化学,1996,13(05):56-57. |
| [10] | 郭广生,刘颖荣,王志华.单分散ZnS颗粒制备参数的研究[J].北京化工大学学报,2000(02):56. |
| [11] | 李道华;叶向荣;忻新泉 .纳米材料的室温(湿)固相化学反应合成[J].化学研究与应用,1999,11(04):415-418. |
| [12] | 杨桦;王子忱;宋利珠 等.发光材料掺锰硫化锌纳米晶的合成与结构表征[J].功能材料,1996,27(04):302-304. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%