为了提高粘胶基碳纤维与树脂的界面粘接性能,采用60Coγ-射线辐射接枝方法对粘胶基碳纤维进行表面改性,研究了接枝溶液种类和吸收剂量对接枝率和复合材料界面性能的影响,吸收剂量对碳纤维抗拉强度的影响,利用扫描电子显微镜分析了辐射接枝后碳纤维表面和复合材料剪切断口断裂形貌的变化.结果表明,环氧/丙酮溶液体系是碳纤维辐射接枝改性的理想溶液,在此溶液中辐射,当吸收剂量大于0.1 kGy时,纤维表面的接枝率为4.2%,复合材料的ILSS提高了20%以上;在合适的吸收剂量下辐射可提高碳纤维的抗拉强度;接枝后纤维表面粗糙度明显增大,与树脂的机械锲合作用增强.
参考文献
| [1] | Bismarck A.;Wuertz C.;Spinger J. .Basic surface oxides on carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(7):1019-1027. |
| [2] | RASHKKOVAN I A;KORABELNIKOV Y G .The effect of fiber surface treatment on its strength and adhesion to the matrix[J].Composite Science and Thchnology,1997,57:1017-1022. |
| [3] | Pittman CU;Yue ZR;Gardner S;Wang L;Toghiani H;Leon CA;Jiang W .Surface properties of electrochemically oxidized carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(11):1797-1807. |
| [4] | 杨永岗;贺福;王茂章 等.碳纤维表面处理的新方法-气液双效法[J].材料研究学报,1998,12(02):207-208. |
| [5] | Cheng T H;ZHANG J;YUMITORI S et al.Sizing resin structure and interphase formation in carbon fiber composites[J].Composites,1994,25(07):661-670. |
| [6] | 韩风,黄永秋,潘鼎.电化学氧化表面处理提高粘胶基碳纤维的界面粘结性能[J].合成纤维工业,2001(04):25-28. |
| [7] | 马恒怡,黄玉东,张志谦.碳纤维γ射线辐照处理对其复合材料界面性能的影响[J].材料工程,2000(04):26-29,33. |
| [8] | 马恒怡,黄玉东,张志谦.γ-射线辐照对碳纤维结构的影响[J].高技术通讯,2001(03):101-103,106. |
| [9] | 田军,王齐祖,杨生荣,薛群基.60Coγ射线辐照对碳纤维表面及其复合材料层间剪切强度的影响[J].复合材料学报,1998(04):1-5. |
| [10] | 邓海;杨济活 .高聚物辐射接枝的发展及应用[J].辐射研究与辐射工艺学报,1998,16(02):65-69. |
| [11] | 黄光林;冯雨丁;吴茂良.高分子辐射化学基础[M].成都:四川大学出版社,1993 |
| [12] | 陈文秀;贾丰;包华影 .环氧树脂的辐射效应[J].辐射研究与辐射工艺学报,1995,13(01):42-46. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%