研究了RE-Mg复合变质对准贝氏体铸钢组织和性能的影响.结果表明:经复合变质处理,首先显著地细化了准贝氏体铸钢的晶粒组织,热处理后钢的晶粒度由变质前的4～5/级变为6～7级.其次,净化了熔体,减少夹杂和气体含量,改变了夹杂形态,使之由Ⅱ类变为Ⅰ类球形夹杂.另外还纯化了钢的基体,提高了钢的致密度.大幅度地提高了钢的强韧性和耐磨性.
参考文献
| [1] | 胡汉起;钟雪友;力航 .Ce对高锰钢奥氏体结晶形貌及Mn的枝晶偏析的影响[J].金属学报,1984,20(04):247-253. |
| [2] | EDMONDS D V;COCERANE R C .Structure - property relationships in bainitic steels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1990,21:1527-1540. |
| [3] | SHINYA T;TOMITA Y .Effect of calcium treatments and strain rate on reheat cracking of vanadium - modified 2. 25Cr - 1 Mo steel[J].Materials Characterization,1999,43:221-225. |
| [4] | 黄进峰,方鸿生,徐平光,郑燕康.稀土、钛变质对贝氏体铸钢成分偏析及强韧性的影响[J].金属热处理学报,2000(01):32-39. |
| [5] | 杜挺.稀土碱土等元素的物理化学及在材料中的应用[M].北京:科学出版社,1995 |
| [6] | 陈佩芳 .稀土金属在钢中的应用[J].金属学报,1978,14(02):188-212. |
| [7] | Sandvik B P J;NEVALAINEN H P.Structure -property relationships in commercial low - alloy bainiticaustenitic steel with high strength,ductility and toughness[J].Metals and Technology,1981(06):213-220. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%