利用SEM/EDX和XRD等手段,用热重法对纯Cr于650~850℃在含有少量气态ZnCl2的氧气中的腐蚀行为进行了研究,并从热力学角度探讨了腐蚀机理.结果表明,随着试验温度的升高和混合气氛中ZnCl2体积分数的增加,Cr的腐蚀明显加剧;本文试验条件下试样皆生成疏松的表面腐蚀产物膜;ZnCl2与表面Cr2O3发生反应,不但破坏了试样表面氧化膜的完整性,而且释放出Cl2导致"活化氧化".
参考文献
[1] | Shinata Y;NISHI Y .NaCl-induced accelerated oxidation of chromium[J].Oxidation of Metals,1986,26:201-212. |
[2] | Shu Y H;WANG F H;WU W T .Corrosion behavior of pure Cr with a solid NaCl deposit in O2 plus water vapor[J].Oxidation of Metals,2000,54:457-471. |
[3] | Shinata Y;HARA M;Nakagawa T .Accelerated oxidation of chromium by trace of sodium chloride vapor[J].Materials Transactions-Japan Institute of Metals,1991,32(10):969-972. |
[4] | 李远士,牛焱,吴维.Fe-Cr合金在450℃的KCl及KCCI-ZnCl2盐膜中的腐蚀[J].金属学报,2001(09):961-964. |
[5] | KUBASCHEWSKI O;ALCOCK C B.Metallugical thermochemistry[M].,1979 |
[6] | Shu Y H;WANG F H;WU W T .Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O2 plus water vapor at 500 ~ 700 ℃[J].Oxidation of Metals,1999,52:463-473. |
[7] | Lee Y Y;MCNALLAN M J .Ignition of nickel in environments containing oxygen and chlorine[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18:1099-1107. |
[8] | Sato Y;HARA M;SHINATA Y .Effect of a small amount of hydrogen chloride on high temperature oxidation of chromium[J].Journal of the Japan Institute of Metals,1995,59(10):1036-1040. |
[9] | 李远士,牛焱,吴维(山文).纯Cr和两种含Cr合金在ZnCl2及KCl-ZnCl2盐膜下的腐蚀[J].中国腐蚀与防护学报,2002(01):27-31. |
[10] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%