以WC-TiC-TaC-Co硬质合金、CuZnNi及氧化物La2O3为原料,研制出一种具有高耐磨性和良好抗冲击性能的堆焊材料,利用SEM、TEM、摩擦磨损试验分析了堆焊材料的组织及耐磨性,探讨了稀土氧化物对堆焊材料组织性能的影响.研究结果表明:硬质合金与Cu基合金通过元素扩散形成连接界面;堆焊层耐磨性随硬质合金含量的增加而增加,随载荷的增加而降低;加入LaO3后,基体组织细化,硬质合金与基体的界面上形成微晶过渡区,改善了界面结合强度,堆焊层耐磨性得到提高.
参考文献
| [1] | Voula Vlaehou;Jean-Michel Piau .A new tool for the rheometric study of oil well cement slurries and other settling suspensions[J].Cement and Concrete Research,2000(10):1551-1557. |
| [2] | KEMBAIYAN K T;KESHAVAN Kesh .Combating sever fliud erosion and corrosion of drill bits using thermal spray coating[J].Wear,1995,186:487-492. |
| [3] | MAYER A C .How to select hardsurfacing materials[J].Welding Design and Fabrication,1982,55(10):61-65. |
| [4] | Sue J A;MINIKUS J C;Fang Z G .Hardfacing on steel tooth cutter element Rock bit[P].US 6029759,2000. |
| [5] | 邹序枚.井下钻具碳化钨强化材料进展[J].稀有金属与硬质合金,1995(03):11-18. |
| [6] | Sue J A;FANG Z G;WHITE A C .Rock bit with wearand fracture-resistant hardfacing[P].US 5921330,1999. |
| [7] | Bailey S G;PERROTT C M .Wear processes exhibited by WC-Co rotary cutters in milling[J].Wear,1974,29:117-128. |
| [8] | 石光浅;黄文哲;王兆亭.硬质合金复合材料堆焊焊条的研制及其应用[J].焊接,1984(12):14-17. |
| [9] | 邹序枚 .牙轮钻齿面强化材料失效分析及齿面强化新材料研究[J].硬质合金,1995,12(03):183-186. |
| [10] | 王新洪 .套磨铣工具强化材料及磨损机制研究[D].山东大学,2001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%