选用TA1钛合金,运用微等离子体氧化技术在其表面原位生长TiO2薄膜.在(Na3PO4-Na2B4O7)电解液体系中,采用XRD、SEM对钛合金表面成膜的微观结构进行测试研究,结果表明:当配比为4:1,成膜时间60min,电流密度10A/dm2条件下制得的薄膜,该膜层中TiO2主要为锐钛矿晶型,膜层均匀,表面粗糙多孔,孔洞大小适中;同时,在电解液中掺杂一定浓度的Fe3+、Si4+离子,当掺杂量分别为0.1～0.2g/L、0.5～1.0g/L条件下制备的薄膜,用于光催化氧化降解水中的罗丹明B,可以提高其光催化活性.
参考文献
| [1] | 李宣东,李垚,刘惠玲,姜兆华,吴晓宏.固定态TiO2薄膜制备及光催化氧化性能研究[J].哈尔滨工业大学学报,2004(01):79-83. |
| [2] | RossH;Bending J;HechtS .SensitizedPhotocatalyticalOxidationof Terbutylazine[J].Solar Energy Materials and Solar Cells,1994,33:475-479. |
| [3] | Li XZ;LIU HL;YUE PT .Photoelectrocatalytic oxida tion of rose bengal in aqueous solution using a Ti/TiO2 mesh electrode[J].Environmental Science and Technology,2000,34(11):4401-4406. |
| [4] | DTTRICH K H;KRYSMANN W;KURZE P et al.Structure and Properties of ANOF Layers[J].Crystal Research and Technology,1984,19(01):93-101. |
| [5] | Krysmann W;KURZE P;DTTRICH K H et al.Process Characteristics and Parameters of Anodic Oxidation by Spark Discharge (ANOF)[J].Crystal Research and Technology,1984,19(07):973-979. |
| [6] | 薛文彬,邓志威,来永春.LY12铝合金微弧氧化的尺寸变化规律[J].中国有色金属学报,1997(03):140-143. |
| [7] | Van T B et al.Brown S. D Mechanism of Aondic SparkDeposition[J].American Ceramic Society Bulletin,1977,56(06):563-566. |
| [8] | 姜兆华,吴晓宏,王福平,辛世刚.Na3PO4-Na2B4O7 体系中钛合金微 等离子体氧化陶瓷膜研究[J].稀有金属,2001(02):151-153. |
| [9] | 张彭义;余刚;蒋展鹏 .半导体光催化剂及其改性技术进展[J].环境污染治理技术与设备,1997,5(03):1-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%