为提高钛基二氧化锡电极的稳定性,设计并制备了含Co中间层的钛基二氧化锡电催化电极Ti/Co/SnO2,以苯酚为目标有机物,考察了所制备Ti/Co/SnO2电极电催化氧化降解苯酚的性能,并采用SEM、EDX以及XPS等检测方法分析了Ti/Co/SnO2电极表面的形貌、元素组成及元素化学态.研究结果表明,含有中间层的Ti/Co/SnO2电极其使用寿命较不含中间层的钛基二氧化锡电极Ti/SnO2大幅度提高,但其对苯酚的电催化降解活性有所下降,氧化还原电对Co2+/Co3+的存在是所制备Ti/Co/SnO2电极稳定性及电催化活性改变的主要原因.
参考文献
| [1] | FENGYJ;LI X Y .Electro-catalyticoxidationofphenolonseveralmetal-oxideselectrodesinaqueoussolution[J].Water Research,2003,36(10):2399-2407. |
| [2] | RILLASE;BASTIDA R M;LLISA E .Electrochemicaldestructionofanilineand4-chloroanilineforwastewatertreatmentusingacarbon-PTEFO2-fedcathode[J].Journal of the Electrochemical Society,1995,142(06):1733-1741. |
| [3] | STUCKIS;KOTZ R;CARCEr B.Electrochemical waste water treatment using high overvoltage anodesPart Ⅱ: Anode performance and application[J].Journal of Applied Electrochemistry,1991(21):99-104. |
| [4] | EERH .Electrodes and Coating thereof[P].US 3632498,1972. |
| [5] | 黄永昌 .钛基金属氧化物电极[J].腐蚀与防护,1999,20(05):251-251. |
| [6] | 冯玉杰,沈宏,崔玉虹,刘峻峰.钛基二氧化铅电催化电极的制备及电催化性能研究[J].分子催化,2002(03):181-186. |
| [7] | 冯玉杰,崔玉虹,孙丽欣,刘峻峰,蔡伟民.电化学废水处理技术及高效电催化电极的研究与进展[J].哈尔滨工业大学学报,2004(04):450-455. |
| [8] | CORREA-LOZANO;COMNINELLIS Ch;DE BATTISTIA.ServicelifeofTi/SnO2-Sb2O5anodes[J].Journal of Applied Electrochemistry,1997(27):970-974. |
| [9] | FENGYu-jie;LI Xiao-yan.Electrochemical degradation of phenol: performance of several metal oxide-based anodes[A].Washington DC,2001:25-29. |
| [10] | 梁镇海,孙彦平.Ti/SnO2+Sb2O3+MnO2/PbO2阳极的性能研究[J].无机材料学报,2001(01):183-187. |
| [11] | 李耀刚.硫酸介质中Ti/SnO2/PbO2析氧阳极的研究[J].电化学,1998(04):439. |
| [12] | 张招贤.钛电极工学[M].北京:冶金工业出版社,2000 |
| [13] | 邹忠 .钛基稀土掺杂金属阳极涂层的催化性能及抗钝化问题研究[D].中南工业大学,1997. |
| [14] | 国家环保局.水和废水监测分析方法[M].北京:中国环境出版社,1998 |
| [15] | 刘业翔.功能电极材料及其应用[M].长沙:中南科技大学出版社,1996 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%