为了丰富CuCr合金的高温腐蚀研究,扩大其应用,采用金相、X射线衍射、扫描电镜/能谱及热重分析法研究了CuCr合金在700~900℃NaCl盐膜下的腐蚀行为,并讨论了在该环境下变形对CuCr合金腐蚀的影响及NaCl加速CuCr合金腐蚀作用的机制.结果表明:合金在NaCl盐膜下发生严重的腐蚀,其腐蚀产物疏松且易剥落,Cr相较Cu易腐蚀,且在腐蚀区以下的合金基体中有贫铬现象,变形能加速CuCr合金的腐蚀速率.
参考文献
[1] | Slade P G .Advances in material development for high power vacuum interrupter contacts[J].IEEE Transactions on Components Packaging and Manufacturing Technology,1994,17:96-106. |
[2] | 傅艳,牛焱,吴维.Cu-Cr合金在H2-H2S混合气中的腐蚀行为[J].中国有色金属学报,2001(04):562-566. |
[3] | ZHANG Cheng-yu,WANG Jiang,ZHANG Hui,YANG Zhi-mao,DING Bing-jun.Deoxidization of CuCr25 alloys prepared by vacuum induction melting[J].中国有色金属学会会刊(英文版),2001(03):337-339. |
[4] | CHIANG T K;AMPAYA J P .Oxidation kinetics of Cu -30vol. % Cr coating[J].Surface and Coatings Technology,1996,78:243-247. |
[5] | FU Guang-yan,NIU Yan,WU Wei-tao,GUAN Heng-rong.Oxidation of two-phase Cu-Cr alloys with different microstructures[J].中国有色金属学会会刊(英文版),2001(03):333-336. |
[6] | K. T. Chiang .Hot gas erosion resistance of a vapor-deposited Cu-Cr coating[J].Surface & Coatings Technology,1999(1):1-6. |
[7] | Walter, RJ;Chiang, KT .Creep of uncoated and Cu-Cr coated NARloy-Z[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(1):8-14. |
[8] | 舒勇华,王福会,吴维(山文).NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响[J].中国腐蚀与防护学报,2000(02):88-96. |
[9] | 梁英教;车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993 |
[10] | 李远士,牛焱,吴维(山文).纯Cr和两种含Cr合金在ZnCl2及KCl-ZnCl2盐膜下的腐蚀[J].中国腐蚀与防护学报,2002(01):27-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%