为研究形变强化工艺对93W-4.9Ni-2.1Fe性能的影响,采用大变形量旋转锻造工艺制备了93W-4.9Ni-2.1Fe合金,并利用SEM与TEM技术分析了旋转锻造态93W-4.9Ni-2.1Fe合金显微组织的形态与尺寸.结果表明:钨合金材料经形变强化后,钨晶粒内部出现由高密度位错形成的胞状组织以及长条状形变晶粒,且粘结相内位错密度较高;旋锻态93W-4.9Ni-2.1Fe合金在具有高强度的同时,保持着一定的延性;旋锻态钨合金的力学性能与变形量及粘结相的分布有关.
参考文献
| [1] | Goren-Muginstein G R;ROSEN A .The effect of cold deformation on grain refinement of heavy metals[J].Materials Science and Engineering,1997,238:351-356. |
| [2] | Gurwell W E .70%Tungstenheavyalloys:Processingandproperties[R].,1991. |
| [3] | Liang G X;WANG E D.Influenceofhotextrusiononmicrostructureandmechanicalpropertiesoftungstenbasedheavyalloy[J].Materials Science and Technology,1996:1032-1034. |
| [4] | R. Gero;L. Borukhin;I. Pikus .Some structural effects of plastic deformation on tungsten heavy metal alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1):162-167. |
| [5] | Zhang Zhaohui;Wang Fuchi .Research on the deformation strengthening mechanism of a tungsten heavy alloy by hydrostatic extrusion[J].International Journal of Refractory Metals & Hard Materials,2001(3):177-182. |
| [6] | Fang Wenbin;WANG Erde;HU Lianxi et al.Microstructureandmechanicalpropertiesofhighdensitytungstenalloyanditsinfluencefactors[J].Transactions of Nonferrous Metals Society of China,2003,13(zk):75-79. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%