采用扩散焊技术对Fe3Al金属间化合物与Q235碳钢进行焊接,研究了Fe3Al/Q235扩散焊界面的剪切强度,并利用扫描电镜分析了界面断裂特征.结果表明,Fe3Al/Q235扩散焊界面断裂位置靠近Fe3Al一侧,剪切断口为解理断裂,伴随少量的韧性断裂特征,微裂纹多数沿靠近Fe3Al一侧的界面交界线扩展,有时偏向界面中心;控制加热温度1060℃,保温45～60min,压力12～15 MPa时,可以获得界面结合紧密、剪切强度112.3 MPa的Fe3Al/Q235接头.
参考文献
| [1] | DAVID S A;HORTON J A;MCKAMEY C G et al.Welding of iron aluminides[J].Welding Journal,1989,68(09):372-381. |
| [2] | DAVID S A;ZACHARIA T .Weldability of Fe3Al-type aluminide[J].Welding Journal,1993,72(05):201-207. |
| [3] | 高德春,杨王玥,董敏,黄继华,孙祖庆.Fe-Al基金属间化合物的焊接性[J].金属学报,2000(01):87-92. |
| [4] | 李亚江,王娟,尹衍升,吴会强,冯吉才.Fe3Al/Q235异种材料扩散焊界面相结构分析[J].焊接学报,2002(02):25-28. |
| [5] | Y.-J. Li;H.-Q. Wu;J. Wang .Characterisation of interface in diffusion bonded Fe_3Al/Q235 carbon steel dissimilar material[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(2):227-230. |
| [6] | YOO M H;FU C L .Cleavage fracture of ordered intermetallic alloys[J].Materials Science and Engineering,1992,153A(1-2):470-478. |
| [7] | NAGPAL P;BAKER I .Room temperature fracture of Fe-Al alloys[J].Materials Characterization,1991,27(03):167-173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%