通过测定抗拉强度、延伸率、厚度分布系数和面密度分布等参数,对比研究了改进的浸涂导电胶、磁控溅射镍和化学镀镍等不同导电化方法对连续泡沫镍的性能的影响.结果表明:磁控溅射镍、化学镀镍和改进的导电胶法,都可制出性能优异的连续泡沫镍;在瓦特镍溶液中,研究了上述3种导电基体上镍的沉积行为,发现石墨导电胶基体上镍的还原存在明显的欠电位沉积现象.
参考文献
| [1] | 王纪三;刘喜信;李长锁 等.镉镍电池及其制造工艺[P].CN 1032038C,1996-06-12. |
| [2] | ORIA M L;CHACON J;HEMANDEZ J C et al.Metal hydride electrodes and Ni/MH batteries for automotive high power applications[J].Journal of Power Sources,2001,102(1-2):97-104. |
| [3] | MARRACINO J M;COEURET F;LANGLOIS S .A first investigation of through porous electrodes made of metallic felts or foams[J].Electrochimica Acta,1987,32(09):1303-1309. |
| [4] | KAMIJO E;MURAKAMI K;TANI K .Process for continuous production of porous metal[P].US 4326931,1982-04-27. |
| [5] | 石殿普;张丽芳;李文明 .一种海绵泡沫镍的制备方法[P].CN 1040237C,1998-10-14. |
| [6] | FERRIER D;MARTINEZ R;YAKOBSON E .Process for preparing a non-conductive substrate for electroplaiting[P].US 5536386,1996-07-16. |
| [7] | 戴长松,王殿龙,胡信国,姜兆华,吴宁,丁飞.超声波对泡沫镍抗拉强度和延伸率的影响[J].材料科学与工艺,2002(04):399-403. |
| [8] | FLINT E B;SUSLICK K S .The Temperature of cavitation[J].Science,1991,253:1397-1399. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%