为提高钛合金的表面耐磨性能,分别以NiCrBSi、NiCrBSi+B4C和B4C+Ti三种材料体系为预涂粉,在Ti-6Al-4V表面涂覆不同厚度的预涂层,采用CO2激光器进行激光熔覆工艺研究.在相同激光熔覆工艺条件下,对不同材料体系的涂层质量进行观察与分析,确认NiCrBSi+B4C材料涂层是三种材料体系中最好的.在激光熔覆过程中,NiCrBSi+B4C材料中的B4C和Ti发生反应,原位生成增强相,对涂层有强化作用.而且,NiCrBSi的加入控制了原位反应的剧烈程度,减少裂纹和气孔,保证了涂层质量.
参考文献
| [1] | Wolfe D.E.;Singh J. .Laser-clad Composite Coatings[J].Advanced Materials & Processes,2000(2):41-44. |
| [2] | Wu X.;Hong Y. .Microstructural Evolution Of A Laser-Cladded Coating[J].Scripta materialia,2000(2):123-127. |
| [3] | PRZYB Ylowicz J;KUSINSKI J .Structure of laser cladded tungsten carbide composite coating[J].Journal of Materials Processing Technology,2001,109:154-160. |
| [4] | J. A. Vreeling;V. Ocelik .Ti-6Al-4V strengthened by laser melt injection of WC_p particles[J].Acta materialia,2002(19):4913-4924. |
| [5] | Sun RL.;Mao JF.;Yang DZ. .Microscopic morphology and distribution of TiC phase in laser clad NiCrBSiC-TiC layer on titanium alloy substrate[J].Surface & Coatings Technology,2002(2/3):203-207. |
| [6] | 杨森,钟敏霖,刘文今.激光熔覆制备原位自生TiC颗粒强化Ni基合金复合涂层的研究[J].航空材料学报,2002(01):26-30. |
| [7] | 唐建新,曾照强,胡晓清,苗赫濯.原位合成TiB2-TiC陶瓷基复合材料[J].材料工程,2001(02):19-21. |
| [8] | 朱春城,林红.TiC-TiB2复合陶瓷的自蔓延高温合成[J].哈尔滨师范大学自然科学学报,2003(01):69-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%