以NiO和Fe2O3为主要原料,研究了其在合成镍铁尖晶石反应烧结过程中的热力学及合成的镍铁尖晶石粉料烧结过程的动力学条件,利用球模型推导的扩散机制的烧结方程测算出不同合成温度烧结试样的烧结机制.同时对在不同烧结温度下合成的尖晶石粉料经二次烧结制备的阳极试样的抗折强度进行了测量.结果表明,NiO和Fe2O3固相反应的热力学条件具备,不同烧结温度烧结的NiFe2O4尖晶石粉料初期烧结由体积扩散和界面扩散共同控制,且当合成尖晶石温度为900℃时,惰性阳极试样气孔率达到一个最小值,此时强度值最大.
参考文献
| [1] | R. P. Pawlek .Recent developments of inert anodes for the primary aluminium industry, Part Ⅰ[J].Aluminium,1995(2):202-206. |
| [2] | 吴贤熙.铝电解惰性阳极研究现状[J].轻金属,2000(01):41-44. |
| [3] | 杨宝刚,于佩志,于先进,邱竹贤.电解铝生产用的惰性电极材料[J].轻金属,2000(05):32-35. |
| [4] | Donald R.Sadoway .Inert Anodes for the Hall-Heroult Cell: The Ultimate Materials Challenge[J].JOM,2001(5):34-35. |
| [5] | OLSEN E;THONSTAD J .Nickel ferrite as inert anodes in aluminum electrolysis:Part Ⅰ Material fabrication and preliminary testing[J].Journal of Applied Electrochemistry,1999,29(03):293-299. |
| [6] | OLSEN E;THONSTAD J .Nickel ferrite as inert anodes in aluminum electrolysis:Part Ⅱ Material fabrication and preliminary testing[J].Journal of Applied Electrochemistry,1999,29(03):301-311. |
| [7] | 梁英教;车荫昌;刘晓霞.无机物热力学数据手册[M].沈阳:东北大学出版社,1993 |
| [8] | H 萨尔满;H 舒尔兹.陶瓷学(上册:基本理论及重要性质)[M].北京:中国轻工业出版社,1989 |
| [9] | 陆佩文.无机材料科学基础(硅酸盐物理化学)[M].武昌:武汉工业大学出版社,1996 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%