通过坩埚下降法制备了单晶锌,同时采用金相实验和XRD分析了所生长的锌单晶,并用塔菲尔曲线外推法、循环伏安法分别研究了锌单晶(002)晶面电极和(100)晶面电极在6.0mol·L-1的KOH溶液中的电化学行为.结果表明:在6.0mol·L-1的KOH溶液中,锌单晶(002)晶面电极的腐蚀速度小于(100)晶面电极;锌单晶(002)晶面电极氧化还原可逆性优于锌单晶(100)晶面电极,锌单晶(100)晶面电极的氧化和还原能力优于锌单晶(002)晶面电极.
参考文献
| [1] | FRANK R;McLarnon;Elton J Cairns .The secondary alkaline zinc electrode[J].J Electrechem Soc,1991,138(02):645-657. |
| [2] | R Renuka;S Ramamurthy;K Muralidharan .Effect of citrate and gluconate ions on the behavior of zinc in 3M NaOH[J].JOURNAL OF POWER SOURCES,1996,78:197-209. |
| [3] | 王建明;钱亚东;张莉 等.可充锌电极存在的问题及解决途径[J].电池,1999,29(02):76-80. |
| [4] | Shin Takahashi;Kiyoshi Hasebe;Akiko Aramata;Akiko Aramata .Anomalous induced anion adsorption on zinc ion underpotential deposition at Au (111) in the presence of halide ions[J].Electrochemistry communications,1999(7):301-304. |
| [5] | Akiko Aramata;Satoshi Taguchi;Toshihiro Fukuda;Mitsuhiro Nakamura;G. Horanyi .Underpotential deposition of zinc ions at single crystal electrodes and the effect of the adsorbed anions[J].Electrochimica Acta,1998(6/7):999-1007. |
| [6] | 杨毅芸,周志有,吴启辉,孙世刚.Sb在Pt（100）, Pt（110）, Pt（111）及Pt（320）上不可逆吸附的电化学特性[J].电化学,2000(03):272-278. |
| [7] | H Nobumistu;T Kimiyoshi;H Shigeta et al.In situ EC-AFM observation with atomic resolution of Pb (100)and Pb(111)single crystals in sulfuric acid solution[J].JOURNAL OF POWER SOURCES,2002,5016:1-6. |
| [8] | 张克从;张乐漶.晶体生长[M].北京:科学出版社,1987 |
| [9] | 周绍民.金属电沉积--原理与研究方法[M].上海:上海科学技术出版社,1987 |
| [10] | 查全性.电极过程动力学导论[M].北京:科学出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%