为了分析ZK60镁合金和Al18B4O33w/ZK60复合材料的高温热变形行为,研究其高温流变应力与应变速率、变形温度之间的关系和组织情况,确定其应变速率敏感指数m和表观激活能Q.利用Gleeble-1500D热模拟试验机,在变形量为60%和不同温度、不同应变速率的条件下对其进行高温热压缩变形.研究表明:在温度为573~673 K和应变速率为0.001~0.1 s-1范围内,镁合金的应变速率敏感指数m值为0.14,复合材料的m值为0.12;合金的表观激活能Q值为226~254 kJ/mol;复合材料的Q值为254~283 kJ/mol.
参考文献
[1] | MORDIKE B L;EBERT T .Magnesium properties-applications-potential[J].Materials Science and Engineering A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2001,302:37-45. |
[2] | VANFLETEREN R .Magnesium for automotive applications[J].Advanced Materials and Processes,1996,5:33-35. |
[3] | Aghion E.;Bronfin B. .Magnesium Alloys Development towards the 21~(st) Century[J].Materials Science Forum,2000(0):19-28. |
[4] | A. GALIYEV;R. KAIBYSHEV;G. GOTTSTEIN .CORRELATION OF PLASTIC DEFORMATION AND DYNAMIC RECRYSTALLIZATION IN MAGNESIUM ALLOY ZK60[J].Acta materialia,2001(7):1199-1207. |
[5] | Arthur Galiyev;Rustam Kaibyshev;Taku Sakai .Continuous Dynamic Recrystallization in Magnesium Alloy[J].Materials Science Forum,2003(Pt.1):509-514. |
[6] | BARNETT M R.Influence of deformation conditions and texture on the high temperature flow stress of magnesium AZ31[J].Journal of Light Metals,2001(01):167-177. |
[7] | M. R. Barnett .Recrystallization During and Following Hot Working of Magnesium Alloy AZ31[J].Materials Science Forum,2003(Pt.1):503-508. |
[8] | Xuyue Yang;Hiromi Miura;Taku Sakai .Dynamic Nucleation of New Grains in Magnesium Alloy during Hot Deformation[J].Materials Science Forum,2003(Pt.1):515-520. |
[9] | J.C. Tan;M.J. Tan .Dynamic continuous recrystallization characteristics in two stage deformation of Mg-3Al-1Zn alloy sheet[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):124-132. |
[10] | 林启权,张辉,彭大暑,林高用,王振球.热压缩2519铝合金流变应力特征[J].矿冶工程,2002(02):110-113. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%