通过原位化学包覆工艺制备的可加工Al2O3/BN纳米复合材料,其抗热震性能明显优于Al2O3基体材料.热震温差△Tc从195℃提高到约395℃,抗热震损伤性能也得到相应的改善.高的抗热震断裂性能源于材料的弹性模量的大幅下降和保持了较高的强度;而优良的抗热震损伤性能则是因为具有弱层间结合的BN易产生大量的微裂纹,屏蔽了热弹性应变能,从而使热震裂纹趋向于准静态扩张.
参考文献
| [1] | 张彪;郭景坤;诸培南.抗热震陶瓷材料的设计[J].硅酸盐通报,1995(03):35-40. |
| [2] | S.W.Lee;D.K.Kim .HIGH TEMPERATURE CHARACTERISTICS OF SI_3N_4/BN FIBROUS MONOLITHIC CERAMICS[J].Ceramic Engineering and Science Proceedings,1997(4):481-486. |
| [3] | TRIPATHI H S;DAS S K;MUKHERJEE B;Ghosh A,Banerjee G. et al.Synthesis and thermo-mechanical properties of mullite-alumina composite derived from sillimanite beach sand:Effect of ZrO2[J].Ceramics International,2001,27(08):833-837. |
| [4] | M. Fellner;P. Supancic .Thermal Shock Failure of Brittle Materials[J].Key engineering materials,2002(223):97-106. |
| [5] | COBLENZ W S;LEWIS Ⅲ D .In situ reaction of B2O3 with AlN and/or Si3N4 to form BN-toughened composites[J].Journal of the American Chemical Society,1988,71(12):1080-1085. |
| [6] | 李永利,乔冠军,金志浩.低温反应制备高纯度纳米BN包覆Al2O3和ZrO2粉体[J].高等学校化学学报,2003(07):1154-1157. |
| [7] | LI Y L;QIAO G J;JIN Z H .Machinable Al2O3/BN Composite Ceramics With Strong Mechanical Properties[J].Materials Research Bulletin,2002,38(07):401-1409. |
| [8] | 张清纯.陶瓷材料的力学性能[M].北京:科学出版社,1987 |
| [9] | 宋世学,艾兴,黄传真.结构陶瓷抗热震性能及其机理的研究进展[J].陶瓷学报,2002(04):233-237. |
| [10] | 陈加庚 .陶瓷材料抗热震断裂性和抗热震损伤性统一的理论[J].中国陶瓷,1995,31(05):31-34. |
| [11] | Rodney W. Trice;John W. Halloran .Influence of microstructure and temperature on the interfacial fracture energy of silicon nitride/boron nitride fibrous monolithic ceramics[J].Journal of the American Ceramic Society,1999(9):2502-2508. |
| [12] | RELLICK G S;ADAMS P M .TEM studies of resinbased matrix microstructure in carbon/carbon composites[J].CARBON,1994,32(01):127-145. |
| [13] | 李永利 .高性能氧化物/BN可加工复相陶瓷的显微结构设计与制备[D].西安交通大学,2003. |
| [14] | 金志浩;高积强;乔冠军.工程陶瓷材料[M].西安:西安交通大学出版社,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%